Organic semiconductor compositions

ABSTRACT

The present invention relates to organic copolymers and organic semiconducting compositions comprising these materials, including layers and devices comprising such organic semiconductor compositions. The invention is also concerned with methods of preparing such organic semiconductor compositions and layers and uses thereof. The invention has application in the field of printed electronics and is particularly useful as a semiconducting material for use in formulations for organic thin film transistor (OTFT) backplanes for displays, integrated circuits, organic light emitting diodes (OLEDs), photodetectors, organic photovoltaic (OPV) cells, sensors, memory elements and logic circuits.

This application is a continuation application of U.S. patentapplication Ser. No. 14/379,801, filed Aug. 20, 2014, which is anational phase application under 35 U.S.C. § 371 of InternationalApplication No. PCT/GB2013/050463, filed Feb. 25, 2013, which claims thebenefit of priority to United Kingdom Patent Application No. 1203159.7,filed Feb. 23, 2012. The entire contents of the above-referenceddisclosures are specifically incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates to organic copolymers and organicsemiconducting compositions comprising these materials, including layersand devices comprising such organic semiconductor compositions. Theinvention is also concerned with methods of preparing such organicsemiconductor compositions and layers and uses thereof. The inventionhas application in the field of printed electronics and is particularlyuseful as a semiconducting material for use in formulations for organicfield effect transistor (OFET) backplanes for displays, integratedcircuits, organic light emitting diodes (OLEDs), photodetectors, organicphotovoltaic (OPV) cells, sensors, memory elements and logic circuits.

BACKGROUND OF THE INVENTION

In recent years, there has been an increasing interest in organicsemiconducting materials as an alternative to conventional silicon-basedsemiconductors. Organic semiconducting materials have several advantagesover those based on silicon, such as lower cost, easier manufacturing,solution processability at low temperatures as well as increasedflexibility, mechanical robustness, good compatibility with a widevariety of flexible substrates and light weight. They thus offer thepossibility of producing more convenient high performance electronicdevices.

Polyacene compounds and their analogues in particular have shown promisein this field of technology. WO 2005/055248 for example, discloses anorganic semiconducting layer formulation comprising an organic binderwhich has a permittivity (c) at 1000 Hz of 3.3 or less, and a polyacenecompound. However the method for preparing the OFETs described in WO2005/055248 in practice is limited and is only useful for producing topgate OFETs having relatively long channel lengths (typically >50microns). A further disadvantage of WO 2005/055248 that is overcome bythe present invention, is that it frequently uses undesirablechlorinated solvents. The highest performance semiconductor compositionsdisclosed in WO 2005/055248 having mobilities ≥1.0 cm²V⁻¹s⁻¹,incorporated 1,2-dichlorobenzene as the solvent (page 54, Table 5 andexamples 14, 21 and 25). Moreover these solvents are not ones that wouldbe industrially acceptable in a printing process and these are alsodamaging to the environment. Therefore it would be desirable to use morebenign solvents for the manufacture of these semiconductor compositions.Furthermore, it is generally thought that only polymer binders with apermittivity of less than 3.3 could be used since any polymers with ahigher permittivity resulted in a very significant reduction in mobilityvalues of the OFET device.

This reduction in mobility value can further be seen in WO 2007/078993which discloses the use of 2,3,9,10-substituted pentacene compounds incombination with insulating polymers having a dielectric constant at1000 Hz of greater than 3.3. These compounds are reported to exhibitmobility values of between 10⁻² and 10⁻⁷ cm²V⁻¹s⁻¹ which are too low tobe industrially useful.

Therefore, the present invention seeks to provide organic semiconductorcompositions, which overcome the above-mentioned problems, by providingsolvent soluble, high mobility, high flexibility polycyclic aromatichydrocarbon copolymers, especiallybenzodichalcogenophenobenzodichalcogenophene ‘BXBX’ copolymers and BXBXanalogue copolymers having a tunable permittivity value and whichexhibit high mobility values.

SUMMARY OF THE INVENTION

The copolymers and compositions of the invention are expected to producesoluble materials that, on deposition, afford flexible, non-brittlelayers unlike layers made from solely small molecule compounds. Thecopolymers of this invention have significantly higher mobilities thantypical semiconducting binders used in the field of printableelectronics, such as the polytriarylamine class of semiconductingbinders that have mobilities in the order of ˜10⁻⁶ to 10⁻³ cm²/Vs. Thecopolymers of the invention will be industrially useful in thefabrication of rollable and flexible electronic devices such as OTFTarrays for displays; large area printed sensors and printed logic. Inparticular, the semiconducting polymers of this invention will be usefulin formulations for organic thin film transistors (OTFTs) having shortchannel lengths 30 microns and even 5 to 10 microns) that may be used asthe backplane driver for electrophoretic displays, high resolution LCDand AMOLED displays.

The copolymers are also soluble in benign, non-chlorinated solvents,such as those typically used in printing.

The present invention also provides highly flexible, non-brittle,semi-conducting films.

Polycyclic Aromatic Hydrocarbon Copolymers (A and B)

Polycyclic Aromatic Hydrocarbon Copolymers (hereinafter PAHCs) accordingto the first aspect of the present invention comprise a mixture of atleast one benzodichalcogenophenobenzodichalcogenophene (hereafterreferred to as BXBX) monomer unit having the Formula (A) and at leastone triarylamine monomer unit having the Formula (B):

whereinY¹ and Y² are independently S or Se;k is 0 or 1l is 0 or 1wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ and R¹²,which may be the same or different, independently represents hydrogen; abranched or unbranched, substituted or unsubstituted C₁-C₄₀ alkyl group;a branched or unbranched, substituted or unsubstituted C₂-C₄₀ alkenylgroup; a branched or unbranched, substituted or unsubstituted C₂-C₄₀alkynyl group; an optionally substituted C₃-C₄₀ cycloalkyl group; anoptionally substituted C₆-C₄₀ aryl group; an optionally substitutedC₁-C₄₀ heterocyclic group; an optionally substituted C₁-C₄₀ heteroarylgroup; an optionally substituted C₁-C₄₀ alkoxy group; an optionallysubstituted C₆-C₄₀ aryloxy group; an optionally substituted C₇-C₄₀alkylaryloxy group; an optionally substituted C₂-C₄₀ alkoxycarbonylgroup; an optionally substituted C₇-C₄₀ aryloxycarbonyl group; a cyanogroup (—CN); a carbamoyl group (—C(═O)NR¹⁵R¹⁶); a carbonyl group(—C(═O)—R¹⁷); a carboxyl group (—CO₂R¹⁸) a cyanate group (—OCN); anisocyano group (—NC); an isocyanate group (—NCO); a thiocyanate group(—SCN) or a thioisocyanate group (—NCS); an optionally substituted aminogroup; a hydroxy group; a nitro group; a CF₃ group; a halo group (Cl,Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰; —SF₅; an optionally substituted silylgroup; a C₂-C₁₀ alkynyl group substituted with a SiH₂R²² group, a C₂-C₁₀alkynyl substituted with a SiHR²²R²³ group, or a C₂-C₁₀ alkynylsubstituted with a —Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group;wherein each R²² group is independently selected from the groupconsisting of a branched or unbranched, substituted or unsubstitutedC₁-C₁₀ alkyl group, a branched or unbranched, substituted orunsubstituted C₂-C₁₀ alkynyl group, a substituted or unsubstitutedC₂-C₂₀ cycloalkyl group, a substituted or unsubstituted C₂-C₁₀ alkenylgroup, and a substituted or unsubstituted C₆-C₂₀ cycloalkylalkylenegroup;each R²³ group is independently selected from the group consisting of abranched or unbranched, substituted or unsubstituted C₁-C₁₀ alkyl group,a branched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup, a substituted or unsubstituted C₂-C₁₀ alkenyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, and a substitutedor unsubstituted C₆-C₂₀ cycloalkylalkylene group;R²⁴ is independently selected from the group consisting of hydrogen, abranched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup, a substituted or unsubstituted C₂-C₂₀ cycloalkyl group, asubstituted or unsubstituted C₆-C₂₀ cycloalkylalkylene group, asubstituted C₅-C₂₀ aryl group, a substituted or unsubstituted C₆-C₂₀arylalkylene group, an acetyl group, a substituted or unsubstitutedC₃-C₂₀ heterocyclic ring comprising at least one of O, N, S and Se inthe ring;wherein x=1 or 2; y=1 or 2; z=0 or 1; and (x+y+z)=3;wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹ and R²⁰ independently represent H oroptionally substituted C₁-C₄₀ carbyl or hydrocarbyl group optionallycomprising one or more heteroatoms;wherein R¹⁷ represents a halogen atom, H or optionally substitutedC₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionally comprising one ormore heteroatoms;wherein at least two of R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, and R¹², are abond, represented by

*, to another monomer unit having the Formula (A) or (B); and whereinAr₁, Ar₂ and Ar₃, which may be the same or different, each represent,independently if in different repeat units, an optionally substitutedC₆₋₄₀ aromatic group (mononuclear or polynuclear), wherein preferably atleast one of Ar₁, Ar₂ and Ar₃ is substituted with at least one polar orpolarising groups and for the monomer group (B),

* represents a bond to another monomer unit having the Formula (A) or(B).

Preferably, k=l=0 or 1.

Preferably k and l=0.

Preferably, x=2 and y=1.

Preferably when z=0, R²² and R²³ together comprise a combination of (i)branched or unbranched, substituted or unsubstituted C₁-C₈ alkylgroup(s) and (ii) branched or unbranched, substituted or unsubstitutedC₂-C₈ alkenyl group(s).

Preferably, any of R²², R²³ and R²⁴ may optionally be substituted with ahalogen atom.

Particularly preferred PAHCs according to the present invention areshown in the following table 1:

TABLE 1 Preferred PAHCs    

  Monomer A

  Monomer B Case 1 Y¹ = Y² are S R′^(a), R′^(b), R′^(c), R′^(d), R′^(e)= H R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R⁴ and R¹⁰ are C₁ to C₁₄alkyl groups, most preferably n-octyl groups. R³ and, R⁹ are bonds toanother unit of Monomer (A) or (B). Case 2 Y¹ = Y² are S R¹, R², R⁵, R⁶,R⁷, R⁸, R¹¹, R¹² are all H. R³ and R⁹ are C₁ to C₁₄ alkyl groups, mostpreferably n-octyl groups. R⁴ and R¹⁰ are bonds to another unit ofMonomer (A) or (B). Case 3 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹,R¹² are all H. R⁴ and R¹⁰ are CF₃ groups. R³ and R⁹ are bonds to anotherunit of Monomer (A) or (B). Case 4 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸,R¹¹, R¹² are all H. R³ and, R⁹ are CF₃ groups. R⁴ and R¹⁰ are bonds toanother unit of Monomer (A) or (B). Case 1 R′^(b), R′^(d), R′^(e) = HCase 2 R′^(a) and R′^(c) = C₁ to C₄ alkyl Case 3 Case 4 Case 1 R′^(b),R′^(c), R′^(d), R′^(e) = H Case 2 R′^(a) = C₁ to C₆ alkoxy Case 3 (i)R′^(a) = methoxy Case 4 (ii) R′^(a) = ethoxy Case 1 R′^(a), R′^(b),R′^(d), R′^(e) = H Case 2 R′^(c) = C₁ to C₆ alkoxy Case 3 (i) R′^(c) =methoxy Case 4 (ii) R′^(c) = ethoxy Case 1 R′^(a), R′^(b), R′^(c),R′^(d) = H Case 2 R′^(e) = C₁ to C₆ alkoxy Case 3 (i) R′^(e) = methoxyCase 4 (ii) R′^(e) = ethoxy Case 1 R′^(b), R′^(d), R′^(e) = H Case 2R′^(a) = R′^(c) = C₁ to C₆ alkoxy Case 3 (i) R′^(a) = R′^(c) = methoxyCase 4 (ii) R′^(a) = R′^(c) = ethoxy Case 1 R′^(b), R′^(d) = H Case 2R′^(a), R′^(c), R′^(e) = C₁ to C₆ alkoxy Case 3 (i) R′^(a), R′^(c),R′^(e) = methoxy Case 4 (ii) R′^(a), R′^(c), R′^(e) = ethoxy Case 1R′^(b), R′^(d) = H Case 2 R′^(b), R′^(c), R′^(d) = C₁ to C₆ alkoxy Case3 (i) R′^(b), R′^(c), R′^(d) = methoxy Case 4 (ii) R′^(b), R′^(c),R′^(d) = ethoxy Case 1 R′^(b), R′^(c), R′^(d), R′^(e) = H Case 2 R′^(a)= Cyano (CN) Case 3 Case 4 Case 1 R′^(b), R′^(c), R′^(d), R′^(e) = HCase 2 R′^(a) = Isopropylcyano group Case 3 Monomer B: Case 4

Case 1 R′^(a), R′^(b), R′^(d), R′^(e) = H Case 2 R′^(c) = Isopropylcyanogroup Case 3 Monomer B: Case 4

The organic semiconductors compounds specified in the table areparticularly preferred as they combine the beneficial properties of highcharge transport mobility (of the binders) with a polarity that is morecompatible with benign, non-chlorinated solvents that will be desirablefor use in large area printing. In addition, as these compounds are morepolar once deposited as the OSC layer, or alternatively as a componentin the OSC layer, they are expected to be resistant to beingre-dissolved by the hydrophobic solvents used for the organic gateinsulators (OGI) such as Cytop. Furthermore, it is expected that thepolar binders are useful for both top gate and bottom gate OTFTs,particularly for bottom gate OTFTs.

The copolymers according to the present invention preferably have anumber average molecular weight (Mn) of between 500 and 100,000, morepreferably between 1600 and 20000, more preferably between 500 and10000, even more preferably between 850 and 5000.

The copolymers according to the present invention preferably havebetween 1 and 100000 monomer units having the Formula (A) and between 1and 100000 triarylamine monomer units having the Formula (B). Morepreferably, the copolymers have between 1 and 1000 monomer units havingthe Formula (A) and between 1 and 1000 triarylamine monomer units havingthe Formula (B). More preferably, the copolymers have between 1 and 100monomer units having the Formula (A) and between 1 and 100 triarylaminemonomer units having the Formula (B). Yet even more preferably, thecopolymers have between 1 and 10 monomer units having the Formula (A)and between 1 and 10 triarylamine monomer units having the Formula (B).

Preferably, the organic semiconductor compositions according to thepresent invention contain less than 10% by weight, more preferably lessthan 5% by weight, more preferably less than 1%, more preferably,substantially no organic binders which have a permittivity at 1000 Hz ofless than 3.4.

Preferred PAHCs and compositions of the present invention contain atleast 20 wt. %, more preferably at least 20-40 wt. % (of the total ofall monomer units (A) and (B) in the copolymer or composition) of aheteroacene monomer unit having the Formula (A) and at least 20 wt. %,preferably at least 20-80 wt. %, more preferably at least 50 wt. %, andeven more preferably at least 60-80 wt. % of a monomer unit having theFormula (B).

Preferred PAHCs and compositions of the present invention contain atleast 40 wt. % (of the total of all monomer units (A) and (B) in thecopolymer or composition) of a BXBX monomer unit having the Formula (A)and at least 40 wt. %, preferably 60 wt. % of a monomer unit having theFormula (B). Preferred PAHCs contain monomer unit (B) as the majorcomponent.

The BXBX copolymers may be produced according to the following generalsynthetic regime. For simplicity, a representative BXBX monomer is shown(no further substitutions are shown, the skilled person understandinghow this can be genericised to the structures shown above) being coupledto a representative triphenylamine monomer. The coupling reaction ispreferably a Yamamoto type coupling (using Nickel chloride, zinc,2,2′-bipyridyl, triphenylphosphine and dimethyl acetamide). However,Suzuki coupling is also possible, although in this case it is preferableto remove the boronic esters from the resulting semiconducting polymer.

wherein α and β are preferably integers of 1-100000; and R is preferablyH or a polar or polarising group as defined below. The halogen endgroups are preferentially reacted either by substitution orhydrogentation.

wherein α and β are preferably integers of 1-100000; and R is preferablyH or a polar or polarising group as defined below. On completion of thecoupling reaction, the halogen and boronic ester end groups arepreferably substituted by other groups, for example by hydrogenationand/or hydrolysis respectively.

Following the polymerization step to form the copolymer of the presentinvention, the copolymer may be cross-linked. Cross-linking may beachieved by any known technique. Examples include the application ofheat and/or moisture, ethylene oxide treatment, UV irradiation, gammasterilisation, electron beam irradiation, and autoclaving.

Thus, according to another aspect of the present invention, there isprovided a process for producing a Polycyclic Aromatic HydrocarbonCopolymer (PAHC) comprising copolymerising a composition containing atleast one BXBX monomer unit selected from the structure A′:

and at least one monomer unit selected from the structure B′:

wherein each of R groups, and k and l have the same general andpreferred meanings as described in relation to the PAHC definitionsabove; wherein Ar₁, Ar₂ and Ar₃, which may be the same or different,each represent an optionally substituted C₆₋₄₀ aromatic group(mononuclear or polynuclear), wherein preferably at least one of Ar₁,Ar₂ and Ar₃ is substituted with at least one polar or more polarisinggroup;wherein X′ is a halogen atom or a cyclic borate group; andwherein Z′ is a halogen atom.

Alternatively, X′ may be a cyclic borate group and then in this case, Z′may be a halogen.

Preferably, the cyclic borate group is

Preferably, the process is carried out in a solvent, preferably anorganic solvent, preferably an aromatic organic solvent.

The compositions of the present invention can comprise additionalcurable monomers, for example, diluent monomers. Examples of suitablematerials include radically curable monomer compounds, such as acrylateand methacrylate monomer compounds. Examples of acrylate andmethacrylate monomers include isobornyl acrylate, isobornylmethacrylate, lauryl acrylate, lauryl methacrylate, isodecylacrylate,isodecylmethacrylate, caprolactone acrylate, 2-phenoxyethyl acrylate,isooctylacrylate, isooctylmethacrylate, butyl acrylate, alkoxylatedlauryl acrylate, ethoxylated nonyl phenol acrylate, ethoxylated nonylphenol methacrylate, ethoxylated hydroxyethyl methacrylate, methoxypolyethylene glycol monoacrylate, methoxy polyethylene glycolmonomethacrylate, tetrahydrofurfuryl methacrylate, as well as mixturesor combinations thereof.

In addition, multifunctional acrylate and methacrylate monomers andoligomers can be included in the compositions as reactive diluents andas materials that can increase the crosslink density of the curedcomposition. Examples of suitable multifunctional acrylate andmethacrylate monomers and oligomers include pentaerythritoltetraacrylate, pentaerythritol tetramethacrylate, 1,2-ethylene glycoldiacrylate, 1,2-ethylene glycol dimethacrylate, 1,6-hexanedioldiacrylate, 1,6-hexanediol dimethacrylate, 1,12-dodecanol diacrylate,1,12-dodecanol dimethacrylate, tris(2-hydroxy ethyl) isocyanuratetriacrylate, propoxylated neopentyl glycol diacrylate, hexanedioldiacrylate, tripropylene glycol diacrylate, dipropylene glycoldiacrylate, ethoxylated bisphenol A diacrylate, ethoxylated bisphenol Adimethacrylate, alkoxylated hexanediol diacrylate, alkoxylatedcyclohexane dimethanol diacrylate, polyethylene glycol diacrylate,polyethylene glycol dimethacrylate, tris (2-hydroxy ethyl) isocyanuratetriacrylate, amine modified polyether acrylates (available as PO 83 F®,LR 8869®, and/or LR 8889® (all available from BASF Corporation),trimethylolpropane triacrylate, glycerol propoxylate triacrylate,dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate,ethoxylated pentaerythritol tetraacrylate (available from Sartomer Co.Inc. as SR 494®), as well as mixtures and combinations thereof. When areactive diluent is added to the composition of the present invention,the reactive diluent is added in any desired or effective amount, in oneembodiment at least about 1 percent by weight of the carrier, at leastabout 35 percent by weight of the carrier, no more than about 98 percentby weight of the carrier, no more than about 75 percent by weight of thecarrier, although the amount of diluent can be outside of these ranges.

Copolymers according to the present invention may have a permittivity at1000 Hz of greater than 1.5, preferably greater than 2, preferablygreater than 3. Particularly preferably, copolymers according to thepresent invention are semiconducting copolymers having a permittivity at1000 Hz of between 1.5 and 8, more preferably between 3.4 and 8. In apreferred embodiment, the polyacene copolymers have a permittivity at1000 Hz of between 3.4 and 7, more preferably between 3.4 and 6.5, yetmore preferably between 3.4 and 4.5 and even more preferably between 3.4and 4.0. Copolymers according to the present invention are preferablysemiconducting copolymers and may have a permittivity at 1000 Hz ofgreater than 3.4, for example greater than 3.8, greater than 4.0,greater than 4.2 and the like.

Preferably, the organic semiconductor compositions according to thepresent invention contain less than 10% by weight, more preferably lessthan 5% by weight, more preferably less than 1% by weight, morepreferably, substantially no copolymers which have a permittivity at1000 Hz of less than 3.4. In a preferred embodiment, the permittivity isdetermined by the method disclosed in WO 2004/102690 or by using themethod disclosed herein, preferably by using the method disclosedherein.

Preferably, the copolymers of the present invention are semiconductingcopolymers having a permittivity at 1000 Hz of between 3.4 and 8. In apreferred embodiment, the copolymers have a permittivity at 1000 Hz ofbetween 3.4 and 7, more preferably between 3.4 and 6.5, and even morepreferably between 3.4 and 4.5. The permittivity of the copolymers canbe measured using any standard method known to those skilled in the art.In a preferred embodiment, the permittivity is determined by the methoddisclosed in WO 2004/102690 or by using the method disclosed herein,preferably by using the method disclosed herein.

Monomer Units of Formula (A)

The following are some preferred characteristics of the BXBX monomerunits defined above as (A).

In a preferred embodiment, at least one (and more preferably 2) ofgroups R¹, R⁶, R⁷, and R¹² are tri-C₁₋₂₀ hydrocarbylsilyl C₁₋₄ alkynylgroups.

Preferably at least one pair of R¹/R⁶ and/or R⁷/R¹² aretrihydrocarbylsilyl ethynyl groups.

In a preferred embodiment, at least one pair of R¹/R⁶ and/or R⁷/R¹² are(trihydrocarbylsilyl)ethynyl- groups, —C≡C—SiR²²R²³R²⁴, wherein R²², R²³and R²⁴ independently represent C₁-C₆ alkyl or C₂-C₆ alkenyl. In a morepreferred embodiment, R²², R²³ and R²⁴ are independently selected fromthe group consisting of methyl, ethyl, propyl, isopropyl, n-butyl,isobutyl, t-butyl, 1-propenyl and 2-propenyl.

In a preferred embodiment, at least one pair of R¹/R⁶ and/or R⁷/R¹² aretrialkylsilyl ethynyl groups, —C≡C—SiR²²R²³R²⁴, wherein R²², R²³ and R²⁴independently represent C₁-C₆ alkyl or C₂-C₆ alkenyl. In a morepreferred embodiment, R²², R²³ and R²⁴ are independently selected fromthe group consisting of methyl, ethyl, propyl, isopropyl, n-butyl,isobutyl, t-butyl 1-propenyl and 2-propenyl.

In yet another preferred embodiment, when k=l=0; R¹, R³, R⁴, R⁶, R⁷, R⁹,R¹⁰ and R¹², independently represent H, C₁-C₁₄ alkyl or C₁-C₆ alkoxy.More preferably, R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰ and R¹² are the same andrepresent H, C₁-C₁₄ alkyl or C₁-C₆ alkoxy. In an even more preferredembodiment, R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰ and R¹² are the same ordifferent and are selected from the group consisting of hydrogen,methyl, ethyl, propyl, n-butyl, isobutyl, t-butyl, n-octyl, methoxy,ethoxy, propyloxy and butyloxy, provided that at least at least one ofeach pair of R³/R⁴ and R⁹/R¹⁹ are a bond, represented by

*, to another monomer unit having the Formula (B)

Preferably, R²², R²³ and R²⁴ are independently selected from the groupconsisting hydrogen, a C₁-C₁₀ alkyl group (preferably C₁-C₄-alkyl andmost preferably methyl, ethyl, n-propyl or isopropyl) which mayoptionally be substituted for example with a halogen atom.

R²² and R²³ are preferably independently selected from the groupconsisting optionally substituted C₁₋₁₀ alkyl group and optionallysubstituted C₂₋₁₀ alkenyl, more preferably C₁-C₆ alkyl or C₂-C₆ alkenyl.A preferred alkyl group in this case is isopropyl.

Examples of the silyl group —Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) include,without limitation, trimethylsilyl, triethylsilyl, tripropylsilyl,dimethylethylsilyl, diethylmethylsilyl, dimethylpropylsilyl,dimethylisopropylsilyl, dipropylmethylsilyl, diisopropylmethylsilyl,dipropylethylsilyl, diisopropylethylsilyl, diethylisopropylsilyl,triisopropylsilyl, trimethoxysilyl, triethoxysilyl, triphenylsilyl,diphenylisopropylsilyl, diisopropylphenylsilyl, diphenylethylsilyl,diethylphenylsilyl, diphenylmethylsilyl, triphenoxysilyl,dimethylmethoxysilyl, dimethylphenoxysilyl, methylmethoxyphenyl, etc.For each example in the foregoing list, the alkyl, aryl or alkoxy groupmay optionally be substituted.

In a preferred embodiment of the first aspect of the invention, PAHCsaccording to the present invention comprise at least one BXBX monomerunit having the Formula (A1):

wherein each of R², R⁵, R⁸ and R¹¹ are hydrogen;At least one pair of of R¹/R⁶ and/or R⁸/R¹¹ are H or trialkylsilylethynyl groups, —C≡C—SiR²²R²³R²⁴, wherein R²², R²³ and R²⁴ independentlyrepresent C₁-C₄ alkyl or C₂-C₄ alkenyl;R³, R⁴, R⁹ and R¹⁰ are independently selected from the group consistingof hydrogen; a branched or unbranched, unsubstituted C₁-C₁₄ alkyl group;C₁-C₆ alkoxy group and C₆-C₁₂ aryloxy group;

Provided that at least one of each pair of R³/R⁴ and R⁹/R¹⁹ are a bond,represented by

*, to another monomer unit having the Formula (A), (A1) or (B) and

wherein k and l are independently 0, or 1, preferably both k and l are0.

In monomer units of Formula (A1), wherein k and l are both 0; R¹/R⁶and/or R⁸/R¹¹ are (trialkylsilyl)ethynyl groups, —C≡C—SiR²²R²³R²⁴,wherein R²², R²³ and R²⁴ are preferably selected from ethyl, n-propyl,isopropyl, 1-propenyl or 2-propenyl; R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, R¹¹and R¹² are independently selected from the group consisting ofhydrogen, methyl, ethyl and methoxy, provided that at least one of eachpair of R³/R⁴ and R⁹/R¹⁰ are a bond, represented by

*, to another monomer unit having the Formula (A), (A1) or (B).

In a more preferred embodiment the BXBX moiety in the PAHC copolymer isa substituted BXBX, wherein each R²² group is independently selectedfrom the group consisting of a branched or unbranched, substituted orunsubstituted C₁-C₈ alkyl group, a substituted or unsubstituted C₂-C₁₂cycloalkyl group, and a substituted or unsubstituted C₆-C₁₂cycloalkylalkylene group; each R²³ group is independently selected fromthe group consisting of a substituted or unsubstituted C₂-C₈ alkenylgroup, a substituted or unsubstituted C₂-C₁₂ cycloalkyl group, and asubstituted or unsubstituted C₆-C₁₂ cycloalkylalkylene group; and R²⁴ isindependently selected from the group consisting of hydrogen, a branchedor unbranched, substituted or unsubstituted C₂-C₈ alkynyl group, asubstituted or unsubstituted C₂-C₁₂ cycloalkyl group, a substituted orunsubstituted C₆-C₁₂ cycloalkylalkylene group, a substituted C₅-C₁₂ arylgroup, a substituted or unsubstituted C₆-C₁₄ arylalkylene group, anacetyl group, a substituted or unsubstituted C₅-C₁₂ heterocyclic ringcomprising at least one of O, N, S and Se in the ring.

Preferred PAHCs and compositions of the present invention contain atleast 20 wt. % (of the total of all monomer units (A), (A1) and (B), inthe copolymer or composition) of a BXBX monomer unit having the Formula(A1) and at least 20 wt. %, preferably between 20-80 wt. % of a monomerunit having the Formula (B).

Especially preferred BXBX monomer units according to the presentinvention are those of Formulae (A2)

Preferably Y¹═Y²═S

R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰ and R¹² are the same or different and areindependently selected from the group consisting of hydrogen, methyl,ethyl, propyl, n-butyl, isobutyl, t-butyl, n-octyl, methoxy, ethoxy,propyloxy and butyloxy, more preferably hydrogen, methyl, propyl andmethoxy.

In monomer units of Formula (A2), R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰ and R¹²are independently selected from the group consisting of H, C₁-C₁₄ alkyland C₁-C₆ alkoxy, provided that at least one of each pair of R³/R⁴ andR⁹/R¹⁰ are a bond, represented by

*, to another monomer unit having the Formula (A), (A1), (A2) or (B). Ina preferred embodiment, R³, R⁴, R⁹ and R¹⁰ are the same or different andare independently selected from the group consisting of hydrogen,methyl, ethyl, propyl, n-butyl, isobutyl, t-butyl, n-octyl, methoxy,ethoxy, propyloxy and butyloxy, more preferably hydrogen, methyl, ethyl,propyl, n-octyl and methoxy, provided that at least one of each pair ofR³/R⁴ and R⁹/R¹⁰ are a bond, represented by

*, to another monomer unit having the Formula (A), (A1), (A2), or (B).

In monomer units of Formula (A2), R²⁵, R²⁶ and R²⁷ are independentlyselected from the group consisting of C₁-C₆ alkyl and C₂-C₆ alkenyl,preferably R²⁵, R²⁶ and R²⁷ are independently selected from the groupconsisting of methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl,t-butyl, 1-propenyl and 2-propenyl, more preferably ethyl, n-propyl andisopropyl.

Preferred PAHCs and compositions of the present invention contain atleast 20 wt. % (of the total of all monomer units in the copolymer orcomposition) of a BXBX monomer unit having the Formula (A2) and at least20 wt. %, preferably between 20-80 wt. % of a monomer unit having theFormula (B).

The “R” substituents (that is R¹, R², etc) denote the substituents atthe positions of the heteroacene according to conventional nomenclature:

BXBX monomers according to the present invention may be synthesised byany known method within the common general knowledge of a person skilledin the art. In a preferred embodiment, methods disclosed in EP 2098527,EP 2254171, in the journal eterocycles, 2011, Volume 83, pages 1187 andin Zh. Org. Khim, 1980, Volume 16, pages 384, 425 and 430, can beemployed for the synthesis of heteroacene compounds used in the presentinvention. High permittivity analogues of the PAHCs of the invention maybe prepared according to WO2012/160383 and WO2012/164282.

Monomer Units (B)

The following are some preferred characteristics of the triarylaminemonomer unit defined above as (B),

Preferably, in monomer unit (B), Ar₁, Ar₂ and Ar₃, which may be the sameor different, each represent, independently if in different repeatunits, an optionally substituted C₆₋₂₀ aromatic group (mononuclear orpolynuclear), wherein at least one of Ar₁, Ar₂ and Ar₃ is substitutedwith at least one polar or more polarising group, and n=1 to 100,preferably 1 to 50, preferably 1 to 20, even more preferably 1 to 10 andmore preferably 1 to 5, wherein n refers to the number of monomer units.Preferably, at least one of Ar₁, Ar₂ and Ar₃ is substituted with 1, 2,3, or 4, more preferably 1, 2 or 3, more preferably 1 or 2, preferably 1polar or more polarising group(s).

In a preferred embodiment, the one or more polar or polarising group(s)is independently selected from the group consisting of nitro group,nitrile group, C₁₋₄₀ alkyl group substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; C₁₋₄₀ alkoxy group optionally substitutedwith a nitro group, a nitrile group, a cyanate group, an isocyanategroup, a thiocyanate group or a thioisocyanate group; C₁₋₄₀ carboxylicacid group optionally substituted with a nitro group, a nitrile group, acyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; C₂₋₄₀ carboxylic acid ester optionally substitutedwith a nitro group, a nitrile group, a cyanate group, an isocyanategroup, a thiocyanate group or a thioisocyanate group; sulfonic acidoptionally substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; sulfonic acid ester optionally substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; cyanate group, isocyanate group, thiocyanategroup, thioisocyanate group; and an amino group optionally substitutedwith a nitro group, a nitrile group, a cyanate group, an isocyanategroup, a thiocyanate group or a thioisocyanate group; and combinationsthereof.

In a more preferred embodiment, the one or more polar or polarisinggroup(s) is independently selected from the group consisting of nitrogroup, nitrile group, C₁₋₁₀ alkyl group substituted with a nitrilegroup, a cyanate group, or an isocyanate group; C₁₋₂₀ alkoxy group,C₁₋₂₀ carboxylic acid group, C₂₋₂₀ carboxylic acid ester; sulfonic acidester; cyanate group, isocyanate group, thiocyanate group,thioisocyanate group, and an amino group; and combinations thereof.

More preferably the polar or polarizing group is selected from the groupconsisting of C₁₋₄ cyanoalkyl group, C₁₋₁₀ alkoxy group, nitrile groupand combinations thereof.

More preferably the polar or polarizing group(s) is selected from thegroup consisting of cyanomethyl, cyanoethyl, cyanopropyl, cyanobutyl,methoxy, ethoxy, propoxy, butoxy, nitrile, NH₂ and combinations thereof.Preferably at least one of Ar₁, Ar₂ and Ara is substituted with 1 or 2polar or more polarising group, which may be the same or different.

Yet more preferably, polar or polarizing group(s) is selected from thegroup consisting of isopropyl cyano, cyclohexylcyano, methoxy, ethoxy,nitrile and combinations thereof. Preferably at least one of Ar₁, Ar₂and Ar₃ is substituted with 1 or 2 polar or more polarising group, whichmay be the same or different.

More preferably, polar or polarizing group(s) is selected from the groupconsisting of methoxy, ethoxy, propoxy, butoxy and combinations thereof,wherein at least one of Ar₁, Ar₂ and Ar₃ is substituted with 1 or 2polar or more polarising group, which may be the same or different.

More preferably, polar or polarizing group(s) is selected from the groupconsisting of methoxy and ethoxy, wherein at least one of Ar₁, Ar₂ andAr₃ is substituted with 1 or 2 of the same polar or more polarisinggroup.

In the context of Ar₁, Ar₂ and Ar₃, a mononuclear aromatic group hasonly one aromatic ring, for example phenyl or phenylene. A polynucleararomatic group has two or more aromatic rings which may be fused (forexample napthyl or naphthylene), individually covalently linked (forexample biphenyl) and/or a combination of both fused and individuallylinked aromatic rings. Preferably each Ar₁, Ar₂ and Ar₃ is an aromaticgroup which is substantially conjugated over substantially the wholegroup.

Preferably, Ar₁, Ar₂ and Ar₃, are independently selected from the groupconsisting of C₆₋₂₀ aryl, C₇₋₂₀ aralkyl and C₇₋₂₀ alkaryl, any of whichmay be substituted with 1, 2, or 3 groups independently selected fromC₁₋₄ alkoxy, C₃₋₂₀ cycloalkylcyano, C₁₋₄ cyanoalkyl, CN and mixturesthereof, and n=1 to 10, wherein n refers to the number of monomer units.

Preferably, Ar₁, Ar₂ and Ar₃, are independently selected from the groupconsisting of C₆₋₁₀ aryl, C₇₋₁₂ aralkyl and C₇₋₁₂ alkaryl, any of whichmay be substituted with 1, 2, or 3 groups independently selected fromC₁₋₂ alkoxy, C₁₋₃ cyanoalkyl, CN and mixtures thereof, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are independently selected from the groupconsisting of C₆₋₂₀ aryl, substituted with 1 or 2 groups independentlyselected from C₁₋₄ alkoxy, C₃₋₂₀ cycloalkylcyano, C₁₋₄ cyanoalkyl, CNand mixtures thereof, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are independently selected from the groupconsisting of C₆₋₁₀ aryl, wherein Ar₃, is substituted with 1 or 2 C₁₋₄alkoxy, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are independently selected from the groupconsisting of C₆₋₁₀ aryl, wherein Ar₃ is substituted with 1 C₁₋₄ alkoxy,and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are independently selected from the groupconsisting of phenyl, benzyl, tolyl and naphthyl, any of which may besubstituted with 1, 2 or 3 groups independently selected from methoxy,ethoxy, cyanomethyl, cyanoethyl, CN and mixtures thereof, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are all phenyl, wherein Ar₃ is substitutedwith 1 or 2 C₁₋₄ alkoxy, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are all phenyl which may be independentlysubstituted with 1, 2 or 3 groups selected from methoxy, ethoxy,isoprorylcyano, cyanomethyl, cyanoethyl, CN and mixtures thereof, andn=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are all phenyl which may be independentlysubstituted with 1 or 2 groups selected from methoxy, ethoxy,cyanomethyl, CN and mixtures thereof, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are all phenyl which may be independentlysubstituted with 1 or 2 groups selected from methoxy, ethoxy andmixtures thereof, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are all phenyl which may be independentlysubstituted with 2,4-dimethoxy, 2-cyano, 2-methoxy, 2-ethoxy, 4-methoxy,4-ethoxy, 4-isopropylcyano and 4-cyclohexylcyano, and n=1 to 10.

Preferably, Ar₁, Ar₂ and Ar₃, are all phenyl which may be independentlysubstituted with 2,4-dimethoxy, 2-methoxy, 2-ethoxy, 4-methoxy and4-ethoxy, and n=1 to 10.

The copolymers of the present invention may be a random or blockcopolymer of different monomer units. In such a case, any monomer unitdefined by Formula (A) or (B), may be combined with a different or samemonomer unit of (A) or (B) provided that at least one monomer unit (A)is bonded to at least one monomer unit (B).

The ratio of the monomers in the polycyclic aromatic hydrocarboncopolymers can be altered to allow for adjustment of the permittivityrelative to a homopolymer. Furthermore, preferably the monomer unit of(A) or (B) may be mixed with monomer units which do not meet thedefinition of (A) or (B), provided that the average permittivity of thebinder in the compositions is preferably between 3.4 and 8.0. In thisregard, other suitable monomer units include fluorene monomers such as(C), cis and trans-indenofluorene monomers such as (D and D′) andsprirobifluorene monomers such as (E):

wherein each R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′),each of which may be the same or different, is selected from the samegroup as R¹, R², R³, R⁴, R⁵, R⁶ and R⁷, already defined above.

n′=1 to 3.

When the PAHC according to the present invention comprises one or moremonomers

(C), (D), (D′) and/or (E), the PAHC is comprised of monomer (A) in anamount of at least 20 wt. %; monomer (B) in an amount of at least 60 wt.% and the remainder is comprised of monomers (C), (D), (D′) and/or (E),based on the total weight of all monomer units in the copolymer.

In an even more preferred embodiment of the present invention, themonomer unit (B) comprises at least one unit having the structures (F)to (J):

Polycyclic Aromatic Hydrocarbon Copolymers (A and K)

Polycyclic Aromatic Hydrocarbon Copolymers (hereinafter PAHCs) accordingto a second aspect of the present invention comprise a mixture of atleast one benzodichalcogenophenobenzodichalcogenophene (hereafterreferred to as BXBX) monomer unit having the Formula (A) and at leastone fluorene monomer unit having the Formula (K):

whereinY¹ and Y² are independently S or Se;k is 0 or 1l is 0 or 1wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ and R¹²,which may be the same or different, independently represents hydrogen; abranched or unbranched, substituted or unsubstituted C₁-C₄₀ alkyl group;a branched or unbranched, substituted or unsubstituted C₂-C₄₀ alkenylgroup; a branched or unbranched, substituted or unsubstituted C₂-C₄₀alkynyl group; an optionally substituted C₃-C₄₀ cycloalkyl group; anoptionally substituted C₆-C₄₀ aryl group; an optionally substitutedC₁-C₄₀ heterocyclic group; an optionally substituted C₁-C₄₀ heteroarylgroup; an optionally substituted C₁-C₄₀ alkoxy group; an optionallysubstituted C₆-C₄₀ aryloxy group; an optionally substituted C₇-C₄₀alkylaryloxy group; an optionally substituted C₂-C₄₀ alkoxycarbonylgroup; an optionally substituted C₇-C₄₀ aryloxycarbonyl group; a cyanogroup (—CN); a carbamoyl group (—C(═O)NR¹⁵R¹⁶); a carbonyl group(—C(═O)—R¹⁷); a carboxyl group (—CO₂R¹⁸) a cyanate group (—OCN); anisocyano group (—NC); an isocyanate group (—NCO); a thiocyanate group(—SCN) or a thioisocyanate group (—NCS); an optionally substituted aminogroup; a hydroxy group; a nitro group; a CF₃ group; a halo group (Cl,Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰; —SF₅; an optionally substituted silylgroup; a C₂-C₁₀ alkynyl group substituted with a SiH₂R²² group, a C₂-C₁₀alkynyl substituted with a SiHR²²R²³ group, or a C₂-C₁₀ alkynylsubstituted with a —Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group;wherein each R²² group is independently selected from the groupconsisting of a branched or unbranched, substituted or unsubstitutedC₁-C₁₀ alkyl group, a branched or unbranched, substituted orunsubstituted C₂-C₁₀ alkynyl group, a substituted or unsubstitutedC₂-C₂₀ cycloalkyl group, a substituted or unsubstituted C₂-C₁₀ alkenylgroup, and a substituted or unsubstituted C₆-C₂₀ cycloalkylalkylenegroup;each R²³ group is independently selected from the group consisting of abranched or unbranched, substituted or unsubstituted C₁-C₁₀ alkyl group,a branched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup, a substituted or unsubstituted C₂-C₁₀ alkenyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, and a substitutedor unsubstituted C₆-C₂₀ cycloalkylalkylene group;R²⁴ is independently selected from the group consisting of hydrogen, abranched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup, a substituted or unsubstituted C₂-C₂₀ cycloalkyl group, asubstituted or unsubstituted C₆-C₂₀ cycloalkylalkylene group, asubstituted C₅-C₂₀ aryl group, a substituted or unsubstituted C₆-C₂₀arylalkylene group, an acetyl group, a substituted or unsubstitutedC₃-C₂₀ heterocyclic ring comprising at least one of O, N, S and Se inthe ring;wherein x=1 or 2; y=1 or 2; z=0 or 1; and (x+y+z)=3;wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹ and R²⁰ independently represent H oroptionally substituted C₁-C₄₀ carbyl or hydrocarbyl group optionallycomprising one or more heteroatoms;wherein R¹⁷ represents a halogen atom, H or optionally substitutedC₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionally comprising one ormore heteroatoms;wherein at least two of R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, and R¹², are abond, represented by

*, to another monomer unit having the Formula (A) or (K);wherein each R^(1′), R^(2′), R^(3′) and R^(4′), each of which may be thesame or different, is selected from the same group as R¹, R², R³, R⁴;and wherein preferably at least one of the groups R^(1′), R^(2′),R^(3′), R^(4′) is a polar group or polarising group and for the monomergroup (K),

* represents a bond to another monomer unit having the Formula (A) or(K); andn′=1 to 3.

Preferably, k=l=0 or 1.

Preferably k and l=0.

Preferably, x=2 and y=1.

Preferably when z=0, R²² and R²³ together comprise a combination of (i)branched or unbranched, substituted or unsubstituted C₁-C₈ alkylgroup(s) and (ii) branched or unbranched, substituted or unsubstitutedC₂-C₈ alkenyl group(s).

Preferably, any of R²², R²³ and R²⁴ may optionally be substituted with ahalogen atom.

Particularly preferred PAHCs according to the present invention areshown in the following table 2:

TABLE 2 Preferred PAHCs

  Monomer A      

  Monomer B

  Monomer C Case 1 Y¹ = Y² are S R^(1′) = R^(2′) = C₁ to C₁₄ alkylgroup, R′^(a), R′^(b), R′^(c), R′^(d), R′^(e) = H R¹, R², R⁵, R⁶, R⁷,R⁸, R¹¹, R¹² are all H. preferably n-octyl groups R⁴ and R¹⁰ are C₁ toC₁₄ alkyl groups, most R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; orpreferably n-octyl groups. C₁ to C₄ alkoxy groups; or R³ and, R⁹ arebonds to another unit of Monomer (A) or (B). cyano groups; or isopropylcyano groups. Case 2 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² areall H. R³ and R⁹ are C₁ to C₁₄ alkyl groups, most preferably n-octylgroups. R⁴ and R¹⁰ are bonds to another unit of Monomer (A) or (B). Case3 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R⁴ and R¹⁰are CF₃ groups. R³ and R⁹ are bonds to another unit of Monomer (A) or(B). Case 4 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R³and, R⁹ are CF₃ groups. R⁴ and R¹⁰ are bonds to another unit of Monomer(A) or (B). Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(b),R′^(d), R′^(e) = H Case 2 preferably n-octyl groups R′^(a) and R′^(c) =C₁ to C₄ alkyl Case 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; orCase 4 C₁ to C₄ alkoxy groups; or cyano groups; or isopropyl cyanogroups. Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(b), R′^(c),R′^(d), R′^(e) = H Case 2 preferably n-octyl groups R′^(a) = C₁ to C₆alkoxy Case 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or (i) R′^(a)= methoxy Case 4 C₁ to C₄ alkoxy groups; or (ii) R′^(a) = ethoxy cyanogroups; or isopropyl cyano groups. Case 1 R^(1′) = R^(2′) = C₁ to C₁₄alkyl group, R′^(a), R′^(b), R′^(d), R′^(e) = H Case 2 preferablyn-octyl groups R′^(c) = C₁ to C₆ alkoxy Case 3 R^(3′), R^(4′) = H or C₁to C₄ alkyl groups; or (i) R′^(c) = methoxy Case 4 C₁ to C₄ alkoxygroups; or (ii) R′^(c) = ethoxy cyano groups; or isopropyl cyano groups.Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(a), R′^(b), R′^(c),R′^(d) = H Case 2 preferably n-octyl groups R′^(e) = C₁ to C₆ alkoxyCase 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or (i) R′^(e) =methoxy Case 4 C₁ to C₄ alkoxy groups; or (ii) R′^(e) = ethoxy cyanogroups; or isopropyl cyano groups. Case 1 R^(1′) = R^(2′) = C₁ to C₁₄alkyl group, R′^(b), R′^(d), R′^(e) = H Case 2 preferably n-octyl groupsR′^(a) = R′^(c) = C₁ to C₆ alkoxy Case 3 R^(3′), R^(4′) = H or C₁ to C₄alkyl groups; or (i) R′^(a) = R′^(c) = methoxy Case 4 C₁ to C₄ alkoxygroups; or (ii) R′^(a) = R′^(c) = ethoxy cyano groups; or isopropylcyano groups. Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(b),R′^(d) = H Case 2 preferably n-octyl groups R′^(a), R′^(c), R′^(e) = C₁to C₆ alkoxy Case 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or (i)R′^(a), R′^(c), R′^(e) = methoxy Case 4 C₁ to C₄ alkoxy groups; or (ii)R′^(a), R′^(c), R′^(e) = ethoxy cyano groups; or isopropyl cyano groups.Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(b), R′^(d) = H Case2 preferably n-octyl groups R′^(b), R′^(c), R′^(d) = C₁ to C₆ alkoxyCase 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or (i) R′^(b),R′^(c), R′^(d) = methoxy Case 4 C₁ to C₄ alkoxy groups; or (ii) R′^(b),R′^(c), R′^(d) = ethoxy cyano groups; or isopropyl cyano groups. Case 1R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(b), R′^(c), R′^(d), R′^(e)= H Case 2 preferably n-octyl groups R′^(a) = Cyano (CN) Case 3 R^(3′),R^(4′) = H or C₁ to C₄ alkyl groups; or Case 4 C₁ to C₄ alkoxy groups;or cyano groups; or isopropyl cyano groups. Case 1 R^(1′) = R^(2′) = C₁to C₁₄ alkyl group, R′^(b), R′^(c), R′^(d), R′^(e) = H Case 2 preferablyn-octyl groups R′^(a) = Isopropylcyano group Case 3 R^(3′), R^(4′) = Hor C₁ to C₄ alkyl groups; or Monomer C: Case 4 C₁ to C₄ alkoxy groups;or cyano groups; or isopropyl cyano groups.

Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, R′^(a), R′^(b), R′^(d),R′^(e) = H Case 2 preferably n-octyl groups R′^(c) = Isopropylcyanogroup Case 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or Monomer C:Case 4 C₁ to C₄ alkoxy groups; or cyano groups; or isopropyl cyanogroups.

The organic semiconductors compounds specified in the table areparticularly preferred as they combine the beneficial properties of highcharge transport mobility (of the binders) with a polarity that is morecompatible with benign, non-chlorinated solvents that will be desirablefor use in large area printing. In addition, as these compounds are morepolar once deposited as the OSC layer, or alternatively as a componentin the OSC layer, they are expected to be resistant to beingre-dissolved by the hydrophobic solvents used for the organic gateinsulators (OGI) such as Cytop. Furthermore, it is expected that thepolar binders are useful for both top gate and bottom gate OTFTs,particularly for bottom gate OTFTs.

The copolymers according to the present invention preferably have anumber average molecular weight (Mn) of between 500 and 100,000, morepreferably between 1600 and 20000, more preferably between 500 and10000, even more preferably between 850 and 5000.

The copolymers according to the present invention preferably havebetween 1 and 100000 monomer units having the Formula (A) and between 1and 100000 fluorene monomer units having the Formula (K). Morepreferably, the copolymers have between 1 and 1000 monomer units havingthe Formula (A) and between 1 and 1000 fluorene monomer units having theFormula (K). More preferably, the copolymers have between 1 and 100monomer units having the Formula (A) and between 1 and 100 fluorenemonomer units having the Formula (K). Yet even more preferably, thecopolymers have between 1 and 10 monomer units having the Formula (A)and between 1 and 10 fluorene monomer units having the Formula (K).

Preferably, the organic semiconductor compositions according to thepresent invention contain less than 10% by weight, more preferably lessthan 5% by weight, more preferably less than 1%, more preferably,substantially no organic binders which have a permittivity at 1000 Hz ofless than 3.4.

Preferred PAHCs and compositions of the present invention contain atleast 20 wt. %, more preferably at least 20-40 wt. % (of the total ofall monomer units (A) and (K) in the copolymer or composition) of aheteroacene monomer unit having the Formula (A) and at least 20 wt. %,preferably at least 20-80 wt. %, more preferably at least 50 wt. %, andeven more preferably at least 60-80 wt. % of a monomer unit having theFormula (K).

Preferred PAHCs and compositions of the present invention contain atleast 40 wt. % (of the total of all monomer units (A) and (K) in thecopolymer or composition) of a BXBX monomer unit having the Formula (A)and at least 40 wt. %, preferably 60 wt. % of a monomer unit having theFormula (K). Preferred PAHCs contain monomer unit (K) as the majorcomponent.

The BXBX copolymers may be produced according to the following generalsynthetic regime. For simplicity, a representative BXBX monomer is shown(no further substitutions are shown, the skilled person understandinghow this can be genericised to the structures shown above) being coupledto a representative fluorene monomer. The coupling reaction ispreferably a Yamamoto type coupling (using Nickel chloride, zinc,2,2′-bipyridyl, triphenylphosphine and dimethyl acetamide). However,Suzuki coupling is also possible, although in this case it is preferableto remove the boronic esters from the resulting semiconducting polymer.

wherein α and β are preferably integers of 1-100000; and R′ groups havethe same definition as R^(1′), R^(2′) groups defined below. The halogenend groups are preferentially reacted either by substitution orhydrogentation.

wherein α and β are preferably integers of 1-100000; and R′ groups havethe same definition as R^(1′), R^(2′) groups defined below. Oncompletion of the coupling reaction, the halogen and boronic ester endgroups are preferably substituted by other groups, for example byhydrogenation and/or hydrolysis respectively.

Following the polymerization step to form the copolymer of the presentinvention, the copolymer may be cross-linked. Cross-linking may beachieved by any known technique. Examples include the application ofheat and/or moisture, ethylene oxide treatment, UV irradiation, gammasterilisation, electron beam irradiation, and autoclaving.

Thus, according to another aspect of the present invention, there isprovided a process for producing a Polycyclic Aromatic HydrocarbonCopolymer (PAHC) comprising copolymerising a composition containing atleast one BXBX monomer unit selected from the structure A′:

and at least one monomer unit selected from the structure K′:

wherein each of R groups, and k and l have the same general andpreferred meanings as described in relation to the PAHC definitionsabove; wherein each R^(1′), R^(2′), R^(3′) and R^(4′), each of which maybe the same or different, is selected from the same group as R¹, R², R³,R⁴; and wherein preferably at least one of the groups R^(1′), R^(2′),R^(3′), R^(4′) is a polar group or polarising group and for the monomergroup (K),

* represents a bond to another monomer unit having the Formula (A) or(K); andn′=1 to 3.wherein X′ is a halogen atom or a cyclic borate group; andwherein Z′ is a halogen atom.

Alternatively, X′ may be a cyclic borate group and then in this case, Z′may be a halogen.

Preferably, the cyclic borate group is

Preferably, the process is carried out in a solvent, preferably anorganic solvent, preferably an aromatic organic solvent.

The compositions of the present invention can comprise additionalcurable monomers, for example, diluent monomers. Examples of suitablematerials include radically curable monomer compounds, such as acrylateand methacrylate monomer compounds. Examples of acrylate andmethacrylate monomers include isobornyl acrylate, isobornylmethacrylate, lauryl acrylate, lauryl methacrylate, isodecylacrylate,isodecylmethacrylate, caprolactone acrylate, 2-phenoxyethyl acrylate,isooctylacrylate, isooctylmethacrylate, butyl acrylate, alkoxylatedlauryl acrylate, ethoxylated nonyl phenol acrylate, ethoxylated nonylphenol methacrylate, ethoxylated hydroxyethyl methacrylate, methoxypolyethylene glycol monoacrylate, methoxy polyethylene glycolmonomethacrylate, tetrahydrofurfuryl methacrylate, as well as mixturesor combinations thereof.

In addition, multifunctional acrylate and methacrylate monomers andoligomers can be included in the compositions as reactive diluents andas materials that can increase the crosslink density of the curedcomposition. Examples of suitable multifunctional acrylate andmethacrylate monomers and oligomers include pentaerythritoltetraacrylate, pentaerythritol tetramethacrylate, 1,2-ethylene glycoldiacrylate, 1,2-ethylene glycol dimethacrylate, 1,6-hexanedioldiacrylate, 1,6-hexanediol dimethacrylate, 1,12-dodecanol diacrylate,1,12-dodecanol dimethacrylate, tris(2-hydroxy ethyl) isocyanuratetriacrylate, propoxylated neopentyl glycol diacrylate, hexanedioldiacrylate, tripropylene glycol diacrylate, dipropylene glycoldiacrylate, ethoxylated bisphenol A diacrylate, ethoxylated bisphenol Adimethacrylate, alkoxylated hexanediol diacrylate, alkoxylatedcyclohexane dimethanol diacrylate, polyethylene glycol diacrylate,polyethylene glycol dimethacrylate, tris (2-hydroxy ethyl) isocyanuratetriacrylate, amine modified polyether acrylates (available as PO 83 F®,LR 8869®, and/or LR 8889® (all available from BASF Corporation),trimethylolpropane triacrylate, glycerol propoxylate triacrylate,dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate,ethoxylated pentaerythritol tetraacrylate (available from Sartomer Co.Inc. as SR 494®), as well as mixtures and combinations thereof. When areactive diluent is added to the composition of the present invention,the reactive diluent is added in any desired or effective amount, in oneembodiment at least about 1 percent by weight of the carrier, at leastabout 35 percent by weight of the carrier, no more than about 98 percentby weight of the carrier, no more than about 75 percent by weight of thecarrier, although the amount of diluent can be outside of these ranges.

Copolymers according to the present invention may have a permittivity at1000 Hz of greater than 1.5, preferably greater than 2, preferablygreater than 3. Particularly preferably, copolymers according to thepresent invention are semiconducting copolymers having a permittivity at1000 Hz of between 1.5 and 8, more preferably between 3.4 and 8. In apreferred embodiment, the polyacene copolymers have a permittivity at1000 Hz of between 3.4 and 7, more preferably between 3.4 and 6.5, yetmore preferably between 3.4 and 4.5 and even more preferably between 3.4and 4.0. Copolymers according to the present invention are preferablysemiconducting copolymers and may have a permittivity at 1000 Hz ofgreater than 3.4, for example greater than 3.8, greater than 4.0,greater than 4.2 and the like.

Preferably, the organic semiconductor compositions according to thepresent invention contain less than 10% by weight, more preferably lessthan 5% by weight, more preferably less than 1% by weight, morepreferably, substantially no copolymers which have a permittivity at1000 Hz of less than 3.4. In a preferred embodiment, the permittivity isdetermined by the method disclosed in WO 2004/102690 or by using themethod disclosed herein, preferably by using the method disclosedherein.

Preferably, the copolymers of the present invention are semiconductingcopolymers having a permittivity at 1000 Hz of between 3.4 and 8. In apreferred embodiment, the copolymers have a permittivity at 1000 Hz ofbetween 3.4 and 7, more preferably between 3.4 and 6.5, and even morepreferably between 3.4 and 4.5. The permittivity of the copolymers canbe measured using any standard method known to those skilled in the art.In a preferred embodiment, the permittivity is determined by the methoddisclosed in WO 2004/102690 or by using the method disclosed herein,preferably by using the method disclosed herein.

Monomer Units of Formula (A)

The preferred characteristics of the BXBX monomer units (A) are asdefined above, except that any reference to monomer (B) should beconsidered to be a reference to monomer (K), in accordance with thesecond aspect of the present invention.

Monomer Units (K)

The following are some preferred characteristics of the fluorene monomerunit defined above as (K).

In monomer unit (K), preferably each R^(1′), R^(2′), R^(3′), R^(4′),each of which may be the same or different, is selected from hydrogen; abranched or unbranched, substituted or unsubstituted C₁-C₁₀ alkyl group;a branched or unbranched, substituted or unsubstituted C₂-C₁₀ alkenylgroup; a branched or unbranched, substituted or unsubstituted C₂-C₁₀alkynyl group; an optionally substituted C₃-C₁₀ cycloalkyl group; anoptionally substituted C₆-C₁₀ aryl group; an optionally substitutedC₁-C₁₀ heterocyclic group; an optionally substituted C₁-C₁₀ heteroarylgroup; an optionally substituted C₁-C₁₀ alkoxy group; an optionallysubstituted C₆-C₁₀ aryloxy group; an optionally substituted C₇-C₁₀alkylaryloxy group; an optionally substituted C₂-C₁₀ alkoxycarbonylgroup; an optionally substituted C₇-C₂₀ aryloxycarbonyl group; a cyanogroup (—CN); a carbamoyl group (—C(═O)NR¹⁵R¹⁶); a carbonyl group(—C(═O)—R¹⁷); a carboxyl group (—CO₂R¹⁸) a cyanate group (—OCN); anisocyano group (—NC); an isocyanate group (—NCO); a thiocyanate group(—SCN) or a thioisocyanate group (—NCS); an optionally substituted aminogroup; a hydroxy group; a nitro group; a CF₃ group; a halo group (Cl,Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰; —SF₅; an optionally substituted silylgroup; a C₂-C₁₀ alkynyl group substituted with a SiH₂R²² group, a C₂-C₁₀alkynyl substituted with a SiHR²² R²³ group, or a C₂-C₁₀ alkynylsubstituted with a —Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group, wherein each ofx, y and z, and R¹⁵, R¹⁶, R¹⁸, R¹⁹ and R²⁰, R²², R²³ and R²⁴ are asdefined above.

In monomer unit (K), preferably each R^(1′), R^(2′), R^(3′), R^(4′),each of which may be the same or different, is H, methyl, methoxy,cyano, cyanomethyl, preferably H.

Preferably, in monomer unit (K), at least one of R^(1′), R^(2′), R^(3′)and R^(4′) is a polar group or more polarising group and n=1 to 100,preferably 1 to 50, preferably 1 to 20, even more preferably 1 to 10 andmore preferably 1 to 5, wherein n refers to the number of monomer units.Preferably, at least one of R^(1′), R^(2′), R^(3′) R^(4′), morepreferably at least two of R^(1′), R^(2′), R^(3′) R^(4′) are polargroups or polarising groups.

In a preferred embodiment, the one or more polar or polarising group(s)is independently selected from the group consisting of nitro group,nitrile group, C₁₋₄₀ alkyl group substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; a C₁₋₄₀ alkoxy group optionally substitutedwith a nitro group, a nitrile group, a cyanate group, an isocyanategroup, a thiocyanate group or a thioisocyanate group; a C₁₋₄₀ carboxylicacid group optionally substituted with a nitro group, a nitrile group, acyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; a C₂₋₄₀ carboxylic acid ester optionallysubstituted with a nitro group, a nitrile group, a cyanate group, anisocyanate group, a thiocyanate group or a thioisocyanate group;sulfonic acid optionally substituted with a nitro group, a nitrilegroup, a cyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; sulfonic acid ester optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; cyanate group, isocyanategroup, thiocyanate group, thioisocyanate group; and an amino groupoptionally substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; and combinations thereof.

In a more preferred embodiment, the one or more polar or polarisinggroup(s) is independently selected from the group consisting of nitrogroup, nitrile group, C₁₋₁₀ alkyl group substituted with a nitrilegroup, a cyanate group, or an isocyanate group; C₁₋₂₀ alkoxy group,C₁₋₂₀ carboxylic acid group, C₂₋₂₀ carboxylic acid ester; sulfonic acidester; cyanate group, isocyanate group, thiocyanate group,thioisocyanate group, and an amino group; and combinations thereof.

More preferably the polar or polarizing group is selected from the groupconsisting of C₁₋₄ cyanoalkyl group, C₁₋₁₀ alkoxy group, nitrile groupand combinations thereof.

More preferably the polar or polarizing group(s) is selected from thegroup consisting of cyanomethyl, cyanoethyl, cyanopropyl, cyanobutyl,methoxy, ethoxy, propoxy, butoxy, nitrile, NH₂ and combinations thereof.Preferably at least one of the R^(1′), R^(2′), R^(3′), R^(4′) groups isa polar group or more polarising group, which may be the same ordifferent.

Yet more preferably, the polar or polarizing group(s) is selected fromthe group consisting of isopropyl cyano, cyclohexylcyano, methoxy,ethoxy, nitrile and combinations thereof. Preferably at least one ofR^(1′), R^(2′), R^(3′), R^(4′) is a polar or more polarising group,which may be the same or different.

More preferably, the polar group or polarizing group(s) is selected fromthe group consisting of methoxy, ethoxy, propoxy, butoxy andcombinations thereof, wherein at least one of R^(1′), R^(2′), R^(3′) andR^(4′) is 1 or 2 polar or more polarising group, which may be the sameor different.

More preferably, polar or polarizing group(s) is selected from the groupconsisting of methoxy and ethoxy, wherein at least one of R^(1′),R^(2′), R^(3′), R^(4′) is 1 or 2 of the same polar or more polarisinggroup.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), are independently selectedfrom the groups consisting of C₁₋₂ alkoxy, C₁₋₃ cyanoalkyl, CN andmixtures thereof, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), are independently selectedfrom the group consisting of C₁₋₄ alkoxy, C₃₋₂₀ cycloalkylcyano, C₁₋₄cyanoalkyl, CN and mixtures thereof, and n=1 to 10.

Preferably, R^(3′), is independently selected from the group consistingof 1 C₁₋₄ alkoxy, and n=1 to 10.

Preferably, R^(3′) and R^(4′), are independently selected from the groupconsisting of methoxy, ethoxy, cyanomethyl, cyanoethyl, CN and mixturesthereof, and n=1 to 10.

Preferably, R^(4′) is independently selected from the group consistingof 1 C₁₋₄ alkoxy, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′) are independently selectedfrom methoxy, ethoxy, isopropylcyano, cyanomethyl, cyanoethyl, CN andmixtures thereof, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′) are independently selectedfrom methoxy, ethoxy, cyanomethyl, CN and mixtures thereof, and n=1 to10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′) are independently selectedfrom methoxy, ethoxy and mixtures thereof, and n=1 to 10.

The copolymers of the present invention may be a random or blockcopolymer of different monomer units. In such a case, any monomer unitdefined by Formula (A) or (K), may be combined with a different or samemonomer unit of (A) or (K) provided that at least one monomer unit (A)is bonded to at least one monomer unit (K).

The ratio of the monomers in the polycyclic aromatic hydrocarboncopolymers can be altered to allow for adjustment of the permittivityrelative to a homopolymer. Furthermore, preferably the monomer unit of(A) or (K) may be mixed with monomer units which do not meet thedefinition of (A) or (K), provided that the average permittivity of thebinder in the compositions is preferably between 3.4 and 8.0. In thisregard, other suitable monomer units include arylamine monomers such as(L), cis and trans-indenofluorene monomers such as (M and M′)respectively and sprirobifluorene monomers such as (N):

wherein each R^(1″), R^(2″), R^(3″), R^(4″), R^(5″), R^(6″) and R^(7″),each of which may be the same or different, is selected from the samegroup as R¹ to R⁷, already defined above;Ar₁, Ar₂ and Ar₃, which may be the same or different, each represent,independently an optionally substituted C₆₋₄₀ aromatic group(mononuclear or polynuclear). Preferably at least one of Ar₁, Ar₂ andAr₃ is substituted with at least one polar or more polarising group, andn=1 to 20, preferably 1 to 10 and more preferably 1 to 5. Preferably, atleast one of Ar₁, Ar₂ and Ar₃ is substituted with 1, 2, 3, or 4, morepreferably 1, 2 or 3, more preferably 1 or 2, preferably 1 polar or morepolarising group(s); andn″=1 to 3.

When the PAHC according to the present invention comprises one or moremonomers (L), (M), (M′) and/or (N), the PAHC is comprised of monomer (A)in an amount of at least 20 wt. %; monomer (K) in an amount of at least60 wt. % and the remainder is comprised of monomers (L), (M), (M′)and/or (N), based on the total weight of all monomer units in thecopolymer.

Polycyclic Aromatic Hydrocarbon Copolymers (A and O)

Polycyclic Aromatic Hydrocarbon Copolymers (hereinafter PAHCs) accordingto the present invention comprise a mixture of at least onebenzodichalcogenophenobenzodichalcogenophene (hereafter referred to asBXBX) monomer unit having the Formula (A) and at least one triarylaminemonomer unit having the Formula (O):

Formula (O/O′)-represents cis and/or trans-indenofluorene isomerswherein

Y¹ and Y² are independently S or Se;k is 0 or 1l is 0 or 1wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ and R¹²,which may be the same or different, independently represents hydrogen; abranched or unbranched, substituted or unsubstituted C₁-C₄₀ alkyl group;a branched or unbranched, substituted or unsubstituted C₂-C₄₀ alkenylgroup; a branched or unbranched, substituted or unsubstituted C₂-C₄₀alkynyl group; an optionally substituted C₃-C₄₀ cycloalkyl group; anoptionally substituted C₆-C₄₀ aryl group; an optionally substitutedC₁-C₄₀ heterocyclic group; an optionally substituted C₁-C₄₀ heteroarylgroup; an optionally substituted C₁-C₄₀ alkoxy group; an optionallysubstituted C₆-C₄₀ aryloxy group; an optionally substituted C₇-C₄₀alkylaryloxy group; an optionally substituted C₂-C₄₀ alkoxycarbonylgroup; an optionally substituted C₇-C₄₀ aryloxycarbonyl group; a cyanogroup (—CN); a carbamoyl group (—C(═O)NR¹⁵R¹⁶); a carbonyl group(—C(═O)—R¹⁷); a carboxyl group (—CO₂R¹⁸) a cyanate group (—OCN); anisocyano group (—NC); an isocyanate group (—NCO); a thiocyanate group(—SCN) or a thioisocyanate group (—NCS); an optionally substituted aminogroup; a hydroxy group; a nitro group; a CF₃ group; a halo group (Cl,Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰; —SF₅; an optionally substituted silylgroup; a C₂-C₁₀ alkynyl group substituted with a SiH₂R²² group, a C₂-C₁₀alkynyl substituted with a SiHR²²R²³ group, or a C₂-C₁₀ alkynylsubstituted with a —Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group;wherein each R²² group is independently selected from the groupconsisting of a branched or unbranched, substituted or unsubstitutedC₁-C₁₀ alkyl group, a branched or unbranched, substituted orunsubstituted C₂-C₁₀ alkynyl group, a substituted or unsubstitutedC₂-C₂₀ cycloalkyl group, a substituted or unsubstituted C₂-C₁₀ alkenylgroup, and a substituted or unsubstituted C₆-C₂₀ cycloalkylalkylenegroup;each R²³ group is independently selected from the group consisting of abranched or unbranched, substituted or unsubstituted C₁-C₁₀ alkyl group,a branched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup, a substituted or unsubstituted C₂-C₁₀ alkenyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, and a substitutedor unsubstituted C₆-C₂₀ cycloalkylalkylene group;R²⁴ is independently selected from the group consisting of hydrogen, abranched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup, a substituted or unsubstituted C₂-C₂₀ cycloalkyl group, asubstituted or unsubstituted C₆-C₂₀ cycloalkylalkylene group, asubstituted C₅-C₂₀ aryl group, a substituted or unsubstituted C₆-C₂₀arylalkylene group, an acetyl group, a substituted or unsubstitutedC₃-C₂₀ heterocyclic ring comprising at least one of O, N, S and Se inthe ring;wherein x=1 or 2; y=1 or 2; z=0 or 1; and (x+y+z)=3;wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹ and R²⁰ independently represent H oroptionally substituted C₁-C₄₀ carbyl or hydrocarbyl group optionallycomprising one or more heteroatoms;wherein R¹⁷ represents a halogen atom, H or optionally substitutedC₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionally comprising one ormore heteroatoms;wherein at least two of R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, and R¹², are abond, represented by

*, to another monomer unit having the Formula (A) or (O);wherein monomer (O/O′) is either the cis and/or trans-indenofluorenemonomer and each R^(1′), R^(2′), R^(3′) R^(4′), R^(5′), R^(6′), R^(7′),each of which may be the same or different, is selected from the samegroup as R¹, R², R³, R⁴, R⁶, R⁷ and wherein preferably at least one ofthe groups, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′) isa polar or polarising group and for the monomer group (O/O′)

* represents a bond to another monomer unit having the Formula (A) or(O/O′); andwherein n′=1 to 3.

Preferably, k=l=0 or 1.

Preferably k and l=0

Preferably, x=2 and y=1.

Preferably when z=0, R²² and R²³ together comprise a combination of (i)branched or unbranched, substituted or unsubstituted C₁-C₈ alkylgroup(s) and (ii) branched or unbranched, substituted or unsubstitutedC₂-C₈ alkenyl group(s).

Preferably, any of R²², R²³ and R²⁴ may optionally be substituted with ahalogen atom.

Particularly preferred PAHCs according to the present invention areshown in the following table 3:

TABLE 3 Preferred PAHCs

Case 1 Y¹ = Y² are S R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄alkyl group, R^(′a), R^(′b), R^(′c), R^(′d), R^(′e) = H R¹, R², R⁵, R⁶,R⁷, R⁸, R¹¹, R¹² are all H. preferably n-octyl groups R⁴ and R¹⁰ are C₁to C₁₄ alkyl groups, most preferably R^(5′), R^(6′) and R^(7′) are H orC₁ to C₄ alkyl groups; or C₁ n-octyl groups. to C₄ alkoxy groups; orcyano groups; or R³ and, R⁹ are bonds to another unit of Monomerisopropyl cyano groups. (A) or (B). Case 2 Y¹ = Y² are S R¹, R², R⁵, R⁶,R⁷, R⁸, R¹¹, R¹² are all H. R³ and R⁹ are C₁ to C₁₄ alkyl groups, mostpreferably n-octyl groups. R⁴ and R¹⁰ are bonds to another unit ofMonomer (A) or (B). Case 3 Y¹ = Y² are S R¹, R², R³, R⁶, R⁷, R⁸, R¹¹,R¹² are all H. R⁴ and R¹⁰ are CF₃ groups. R³ and R⁹ are bonds to anotherunit of Monomer (A) or (B). Case 4 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸,R¹¹, R¹² are all H. R³ and, R⁹ are CF₃ groups. R⁴ and R¹⁰ are bonds toanother unit of Monomer (A) or (B). Case 1 R^(1′), R^(2′), R^(3′) andR^(4′) are C₁ to C₁₄ alkyl group, R^(′b), R^(′d), R^(′e) = H Case 2preferably n-octyl groups R^(′a) and R^(′c) = C₁ to Case 3 R^(5′),R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups; or C₁ C₄ alkyl Case 4to C₄ alkoxy groups; or cyano groups; or isopropyl cyano groups. Case 1R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′b),R^(′c), R^(′d), R^(′e) = H Case 2 preferably n-octyl groups R^(′a) = C₁to C₆ Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups;or C₁ alkoxy Case 4 to C₄ alkoxy groups; or cyano groups; or (i) R^(′a)= methoxy isopropyl cyano groups. (ii) R^(′a) = ethoxy Case 1 R^(1′),R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′a), R^(′b),R^(′d), R^(′e) = H Case 2 preferably n-octyl groups R^(′c) = C₁ to C₆Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups; or C₁alkoxy Case 4 to C₄ alkoxy groups; or cyano groups; or (i) R^(′c) =methoxy isopropyl cyano groups. (ii) R^(′c) = ethoxy Case 1 R^(1′),R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′a), R^(′b),R^(′c), R^(′d) = H Case 2 preferably n-octyl groups R^(′e) = C₁ to C₆Case 3 alkoxy Case 4 (i) R^(′e) = methoxy (ii) R^(′e) = ethoxy Case 1R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′b),R^(′d), R^(′e) = H Case 2 preferably n-octyl groups R^(′a) = R^(′c) = C₁to C₆ Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups;or C₁ alkoxy Case 4 to C₄ alkoxy groups; or cyano groups; or (i) R^(′a)= R^(′c) = methoxy isopropyl cyano groups. (ii) R^(′a) = R^(′c) = ethoxyCase 1 R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group,R^(′b), R^(′d) = H Case 2 preferably n-octyl groups R^(′a), R^(′c),R^(′e) = C₁ to Case 3 R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄alkyl group, C₆ alkoxy Case 4 preferably n-octyl groups (i) R^(′a),R^(′c), R^(′e) = methoxy (ii) R^(′a), R^(′c), R^(′e) = ethoxy Case 1R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′a),R^(′e) = H Case 2 preferably n-octyl groups R^(′b), R^(′c), R^(′d) = C₁to Case 3 C₆ alkoxy Case 4 (i) R^(′b), R^(′c), R^(′d) = methoxy (ii)R^(′b), R^(′c), R^(′d) = ethoxy Case 1 R^(′b), R^(′c), R^(′d), R^(′e) =H Case 2 R^(′a) = Cyano (CN) Case 3 Case 4 Case 1 R^(1′), R^(2′), R^(3′)and R^(4′) are C₁ to C₁₄ alkyl group, R^(′b), R^(′c), R^(′d), R^(′e) = HCase 2 preferably n-octyl groups R^(′a) = Case 3 Isopropylcyano Case 4group Monomer C:  

Case 1 R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group,R^(′a), R^(′b), R^(′d), R^(′e) = H Case 2 preferably n-octyl groupsR^(′c) = Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkylgroups; or C₁ lsopropylcyano Case 4 to C₄ alkoxy groups; or cyanogroups; or group isopropyl cyano groups. Monomer C:  

The organic semiconductors compounds specified in the table areparticularly preferred as they combine the beneficial properties of highcharge transport mobility (of the binders) with a polarity that is morecompatible with benign, non-chlorinated solvents that will be desirablefor use in large area printing. In addition, as these compounds are morepolar once deposited as the OSC layer, or alternatively as a componentin the OSC layer, they are expected to be resistant to beingre-dissolved by the hydrophobic solvents used for the organic gateinsulators (OGI) such as Cytop. Furthermore, it is expected that thepolar binders are useful for both top gate and bottom gate OTFTs,particularly for bottom gate OTFTs.

The copolymers according to the present invention preferably have anumber average molecular weight (Mn) of between 500 and 100,000, morepreferably between 1600 and 20000, more preferably between 500 and10000, even more preferably between 850 and 5000.

The copolymers according to the present invention preferably havebetween 1 and 100000 monomer units having the Formula (A) and between 1and 100000 cis/trans-indenofluorene monomer units having the Formula(O). More preferably, the copolymers have between 1 and 1000 monomerunits having the Formula (A) and between 1 and 1000cis/trans-indenofluorene monomer units having the Formula (O). Morepreferably, the copolymers have between 1 and 100 monomer units havingthe Formula (A) and between 1 and 100 cis/trans-indenofluorene unitshaving the Formula (O). Yet even more preferably, the copolymers havebetween 1 and 10 monomer units having the Formula (A) and between 1 and10 cis/trans-indenofluorene monomer units having the Formula (O).

Preferably, the organic semiconductor compositions according to thepresent invention contain less than 10% by weight, more preferably lessthan 5% by weight, more preferably less than 1%, more preferably,substantially no organic binders which have a permittivity at 1000 Hz ofless than 3.4.

Preferred PAHCs and compositions of the present invention contain atleast 20 wt. %, more preferably at least 20-40 wt. % (of the total ofall monomer units (A) and (0) in the copolymer or composition) of aheteroacene monomer unit having the Formula (A) and at least 20 wt. %,preferably at least 20-80 wt. %, more preferably at least 50 wt. %, andeven more preferably at least 60-80 wt. % of a monomer unit having theFormula (O).

Preferred PAHCs and compositions of the present invention contain atleast 40 wt. % (of the total of all monomer units (A) and (O) in thecopolymer or composition) of a BXBX monomer unit having the Formula (A)and at least 40 wt. %, preferably 60 wt. % of a monomer unit having theFormula (O). Preferred PAHCs contain monomer unit (0) as the majorcomponent.

The BXBX copolymers may be produced according to the following generalsynthetic regime. For simplicity, a representative BXBX monomer is shown(no further substitutions are shown, the skilled person understandinghow this can be genericised to the structures shown above) being coupledto a representative cis/trans-indenofluorene monomer. The couplingreaction is preferably a Yamamoto type coupling (using Nickel chloride,zinc, 2,2′-bipyridyl, triphenylphosphine and dimethyl acetamide).However, Suzuki coupling is also possible, although in this case it ispreferable to remove the boronic esters from the resultingsemiconducting polymer.

wherein α and β are preferably integers of 1-100000; R′ has the samedefinition as for R^(1′), R^(2′), R^(3′) and R^(4′) group defined below.The halogen end groups are preferentially reacted either by substitutionor hydrogentation.

wherein α and β are preferably integers of 1-100000; R′ has the samedefinition as for R^(1′), R^(2′), R^(3′) and R^(4′) group defined below.On completion of the coupling reaction, the halogen and boronic esterend groups are preferably substituted by other groups, for example byhydrogenation and/or hydrolysis respectively.

Following the polymerization step to form the copolymer of the presentinvention, the copolymer may be cross-linked. Cross-linking may beachieved by any known technique. Examples include the application ofheat and/or moisture, ethylene oxide treatment, UV irradiation, gammasterilisation, electron beam irradiation, and autoclaving.

Thus, according to another aspect of the present invention, there isprovided a process for producing a Polycyclic Aromatic HydrocarbonCopolymer (PAHC) comprising copolymerising a composition containing atleast one BXBX monomer unit selected from the structure A′:

and at least one monomer unit selected from the structure O′:

wherein each of R and R′ groups, and k and l have the same general andpreferred meanings as described in relation to the PAHC definitionsabove; wherein preferably at least one of and R^(1′), R^(2′), R^(3′),R^(4′), R^(5′), R^(6′), R^(7′) is a polar group or more polarisinggroup; andwherein X′ is a halogen atom or a cyclic borate group; andwherein Z′ is a halogen atom.

Preferably, the cyclic borate group is

Preferably, the process is carried out in a solvent, preferably anorganic solvent, preferably an aromatic organic solvent.

The compositions of the present invention can comprise additionalcurable monomers, for example, diluent monomers. Examples of suitablematerials include radically curable monomer compounds, such as acrylateand methacrylate monomer compounds. Examples of acrylate andmethacrylate monomers include isobornyl acrylate, isobornylmethacrylate, lauryl acrylate, lauryl methacrylate, isodecylacrylate,isodecylmethacrylate, caprolactone acrylate, 2-phenoxyethyl acrylate,isooctylacrylate, isooctylmethacrylate, butyl acrylate, alkoxylatedlauryl acrylate, ethoxylated nonyl phenol acrylate, ethoxylated nonylphenol methacrylate, ethoxylated hydroxyethyl methacrylate, methoxypolyethylene glycol monoacrylate, methoxy polyethylene glycolmonomethacrylate, tetrahydrofurfuryl methacrylate, as well as mixturesor combinations thereof.

In addition, multifunctional acrylate and methacrylate monomers andoligomers can be included in the compositions as reactive diluents andas materials that can increase the crosslink density of the curedcomposition. Examples of suitable multifunctional acrylate andmethacrylate monomers and oligomers include pentaerythritoltetraacrylate, pentaerythritol tetramethacrylate, 1,2-ethylene glycoldiacrylate, 1,2-ethylene glycol dimethacrylate, 1,6-hexanedioldiacrylate, 1,6-hexanediol dimethacrylate, 1,12-dodecanol diacrylate,1,12-dodecanol dimethacrylate, tris(2-hydroxy ethyl) isocyanuratetriacrylate, propoxylated neopentyl glycol diacrylate, hexanedioldiacrylate, tripropylene glycol diacrylate, dipropylene glycoldiacrylate, ethoxylated bisphenol A diacrylate, ethoxylated bisphenol Adimethacrylate, alkoxylated hexanediol diacrylate, alkoxylatedcyclohexane dimethanol diacrylate, polyethylene glycol diacrylate,polyethylene glycol dimethacrylate, tris (2-hydroxy ethyl) isocyanuratetriacrylate, amine modified polyether acrylates (available as PO 83 F®,LR 8869®, and/or LR 8889® (all available from BASF Corporation),trimethylolpropane triacrylate, glycerol propoxylate triacrylate,dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate,ethoxylated pentaerythritol tetraacrylate (available from Sartomer Co.Inc. as SR 494®), as well as mixtures and combinations thereof. When areactive diluent is added to the composition of the present invention,the reactive diluent is added in any desired or effective amount, in oneembodiment at least about 1 percent by weight of the carrier, at leastabout 35 percent by weight of the carrier, no more than about 98 percentby weight of the carrier, no more than about 75 percent by weight of thecarrier, although the amount of diluent can be outside of these ranges.

Copolymers according to the present invention may have a permittivity at1000 Hz of greater than 1.5, preferably greater than 2, preferablygreater than 3. Particularly preferably, copolymers according to thepresent invention are semiconducting copolymers having a permittivity at1000 Hz of between 1.5 and 8, more preferably between 3.4 and 8. In apreferred embodiment, the polyacene copolymers have a permittivity at1000 Hz of between 3.4 and 7, more preferably between 3.4 and 6.5, yetmore preferably between 3.4 and 4.5 and even more preferably between 3.4and 4.0. Copolymers according to the present invention are preferablysemiconducting copolymers and may have a permittivity at 1000 Hz ofgreater than 3.4, for example greater than 3.8, greater than 4.0,greater than 4.2 and the like.

Preferably, the organic semiconductor compositions according to thepresent invention contain less than 10% by weight, more preferably lessthan 5% by weight, more preferably less than 1% by weight, morepreferably, substantially no copolymers which have a permittivity at1000 Hz of less than 3.4. In a preferred embodiment, the permittivity isdetermined by the method disclosed in WO 2004/102690 or by using themethod disclosed herein, preferably by using the method disclosedherein.

Preferably, the copolymers of the present invention are semiconductingcopolymers having a permittivity at 1000 Hz of between 3.4 and 8. In apreferred embodiment, the copolymers have a permittivity at 1000 Hz ofbetween 3.4 and 7, more preferably between 3.4 and 6.5, and even morepreferably between 3.4 and 4.5. The permittivity of the copolymers canbe measured using any standard method known to those skilled in the art.In a preferred embodiment, the permittivity is determined by the methoddisclosed in WO 2004/102690 or by using the method disclosed herein,preferably by using the method disclosed herein.

Monomer Units of Formula (A)

The preferred characteristics of the BXBX monomer units (A) are asdefined above, except that any reference to monomer (B) should beconsidered to be a reference to monomer (O), in accordance with thesecond aspect of the present invention.

Monomer Units (O)/(O′)

The following are some preferred characteristics of thecis/trans-indenofluorene monomer unit defined above as (O)/O′).

In monomer unit (O)/(O′), preferably each R^(1′), R^(2′), R^(3′),R^(4′), R^(5′), R^(6′) and R^(7′), each of which may be the same ordifferent, is selected from hydrogen; a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group; a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkenyl group; abranched or unbranched, substituted or unsubstituted C₂-C₁₀ alkynylgroup; an optionally substituted C₃-C₁₀ cycloalkyl group; an optionallysubstituted C₆-C₁₀ aryl group; an optionally substituted C₁-C₁₀heterocyclic group; an optionally substituted C₁-C₁₀ heteroaryl group;an optionally substituted C₁-C₁₀ alkoxy group; an optionally substitutedC₆-C₁₀ aryloxy group; an optionally substituted C₇-C₁₀ alkylaryloxygroup; an optionally substituted C₂-C₁₀ alkoxycarbonyl group; anoptionally substituted C₇-C₂₀ aryloxycarbonyl group; a cyano group(—CN); a carbamoyl group (—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷);a carboxyl group (—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group(—NC); an isocyanate group (—NCO); a thiocyanate group (—SCN) or athioisocyanate group (—NCS); an optionally substituted amino group; ahydroxy group; a nitro group; a CF₃ group; a halo group (Cl, Br, F, I);—SR¹⁹; —SO₃H; —SO₂R²⁰; —SF₅; an optionally substituted silyl group; aC₂-C₁₀ alkynyl group substituted with a SiH₂R²² group, a C₂-C₁₀ alkynylsubstituted with a SiHR²² R²³ group, or a C₂-C₁₀ alkynyl substitutedwith a —Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group, wherein each of x, y and z,and R¹⁵, R¹⁶, R¹⁸, R¹⁹ and R²⁰, R²², R²³ and R²⁴ are as defined above.

In monomer unit (O)/(O′), preferably each R^(1′), R^(2′), R^(3′),R^(4′), each of which may be the same or different, is H, methyl,methoxy, cyano, cyanomethyl, preferably H.

Preferably, in monomer unit (O)/(O′), at least one of R^(1′), R^(2′),R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′) is a polar or more polarisinggroup and n=1 to 100, preferably 1 to 50, preferably 1 to 20, even morepreferably 1 to 10 and more preferably 1 to 5, wherein n refers to thenumber of monomer units. Preferably, at least one of R^(1′), R^(2′),R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′), more preferably at least twoof R^(1′), R^(2′), R^(3′), R^(4′) R^(5′), R^(6′), R^(7′) are polar orpolarising groups.

In a preferred embodiment, the one or more polar or polarising group(s)is independently selected from the group consisting of nitro group,nitrile group, C₁₋₄₀ alkyl group substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; a C₁₋₄₀ alkoxy group optionally substitutedwith a nitro group, a nitrile group, a cyanate group, an isocyanategroup, a thiocyanate group or a thioisocyanate group; a C₁₋₄₀ carboxylicacid group optionally substituted with a nitro group, a nitrile group, acyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; a C₂₋₄₀ carboxylic acid ester optionallysubstituted with a nitro group, a nitrile group, a cyanate group, anisocyanate group, a thiocyanate group or a thioisocyanate group;sulfonic acid optionally substituted with a nitro group, a nitrilegroup, a cyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; sulfonic acid ester optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; cyanate group, isocyanategroup, thiocyanate group, thioisocyanate group; and an amino groupoptionally substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; and combinations thereof.

In a more preferred embodiment, the one or more polar or polarisinggroup(s) is independently selected from the group consisting of nitrogroup, nitrile group, C₁₋₁₀ alkyl group substituted with a nitrilegroup, a cyanate group, or an isocyanate group; C₁₋₂₀ alkoxy group,C₁₋₂₀ carboxylic acid group, C₂₋₂₀ carboxylic acid ester; sulfonic acidester; cyanate group, isocyanate group, thiocyanate group,thioisocyanate group, and an amino group; and combinations thereof.

More preferably the polar or polarizing group is selected from the groupconsisting of C₁₋₄ cyanoalkyl group, C₁₋₁₀ alkoxy group, nitrile groupand combinations thereof.

More preferably the polar or polarizing group(s) is selected from thegroup consisting of cyanomethyl, cyanoethyl, cyanopropyl, cyanobutyl,methoxy, ethoxy, propoxy, butoxy, nitrile, NH₂ and combinations thereof.Preferably at least one of the R^(1′), R^(2′), R^(3′), R^(4′), R^(5′),R^(6′), R^(7′) groups is a polar or more polarising group, which may bethe same or different.

Yet more preferably, the polar or polarizing group(s) is selected fromthe group consisting of isopropyl cyano, cyclohexylcyano, methoxy,ethoxy, nitrile and combinations thereof. Preferably at least one ofR^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′) is a polar ormore polarising group, which may be the same or different.

More preferably, the polar group or polarizing group(s) is selected fromthe group consisting of methoxy, ethoxy, propoxy, butoxy andcombinations thereof, wherein at least one of R^(1′), R^(2′), R^(3′),R^(4′), R^(5′), R^(6′), R^(7′) is a polar or more polarising group,which may be the same or different.

More preferably, the polar or polarizing group(s) is selected from thegroup consisting of methoxy and ethoxy, wherein at least one of R^(1′),R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′) is the same polar or morepolarising group. Yet more preferably, at least one of R^(5′), R^(6′),R^(7′) is the same polar or more polarising group.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′), areindependently selected from the groups consisting of C₁₋₂ alkoxy, C₁₋₃cyanoalkyl, CN and mixtures thereof, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′), areindependently selected from the group consisting of C₁₋₄ alkoxy, C₃₋₂₀cycloalkylcyano, C₁₋₄ cyanoalkyl, CN and mixtures thereof, and n=1 to10.

Preferably, R^(5′), R^(6′) and R^(7′), is independently selected fromthe group consisting of 1 C₁₋₄ alkoxy, and n=1 to 10.

Preferably, R^(5′), R^(6′) and R^(7′), are independently selected fromthe group consisting of methoxy, ethoxy, cyanomethyl, cyanoethyl, CN andmixtures thereof, and n=1 to 10.

In an even more preferred embodiment of the present invention, themonomer unit (O)/(O′) comprises at least one substituent that ismethoxy, or cyano,

Preferably, R^(4′) is independently selected from the group consistingof 1 C₁₋₄ alkoxy, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′) areindependently selected from methoxy, ethoxy, isopropylcyano,cyanomethyl, cyanoethyl, CN and mixtures thereof, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′) areindependently selected from methoxy, ethoxy, cyanomethyl, CN andmixtures thereof, and n=1 to 10.

Preferably, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′), R^(7′) areindependently selected from methoxy, ethoxy and mixtures thereof, andn=1 to 10.

The copolymers of the present invention may be a random or blockcopolymer of different monomer units. In such a case, any monomer unitdefined by Formula (A) or (O)/(O′), may be combined with a different orsame monomer unit of (A) or (O)/(O′) provided that at least one monomerunit (A) is bonded to at least one monomer unit (O)/(O′).

The ratio of the monomers in the polycyclic aromatic hydrocarboncopolymers can be altered to allow for adjustment of the permittivityrelative to a homopolymer. Furthermore, optionally the monomer unit of(A) or (O)/(O′) may be mixed with monomer units which do not meet thedefinition of (A) or (O)/(O′), provided that the average permittivity ofthe binder in the compositions is preferably between 3.4 and 8.0. Inthis regard, other suitable monomer units include arylamine monomerssuch as (P), fluorene monomers such as (Q) and sprirobifluorene monomerssuch as (R):

wherein each R^(1″) R^(2″), R^(3″) and R^(4″), each of which may be thesame or different, is selected from the same group as R¹, R², R³ and R⁴,already defined above;

Ar₁, Ar₂ and Ar₃, which may be the same or different, each represent,independently an optionally substituted C₆₋₄₀ aromatic group(mononuclear or polynuclear). Preferably at least one of Ar₁, Ar₂ andAr₃ is substituted with at least one polar or more polarising group, andn=1 to 20, preferably 1 to 10 and more preferably 1 to 5. Preferably, atleast one of Ar₁, Ar₂ and Ar₃ is substituted with 1, 2, 3, or 4, morepreferably 1, 2 or 3, more preferably 1 or 2, preferably 1 polar or morepolarising group(s); and

n″=1 to 3.

When the PAHC according to the present invention comprises one or moremonomers (P), (Q) and/or (R), the PAHC is comprised of monomer (A) in anamount of at least 20 wt. %; monomer (O) in an amount of at least 60 wt.% and the remainder is comprised of monomers (P), (Q) and/or (R), basedon the total weight of all monomer units in the copolymer.

Organic Semiconductor Compositions

The present invention is also concerned with organic semiconductorcompositions. In a first aspect of the present invention, the organicsemiconductor composition comprises a PAHC comprising a mixture of atleast one BXBX monomer unit having the Formula (A) and at least onemonomer unit having the Formula (B). In a second aspect of the presentinvention, the organic semiconductor composition comprises a PAHCcomprising a mixture of at least one BXBX monomer unit having theFormula (A) and at least one monomer unit having the Formula (K). In athird aspect of the present invention, the organic semiconductorcomposition comprises a PAHC comprising a mixture of at least one BXBXmonomer unit having the Formula (A) and at least one monomer unit havingthe Formula (O).

An organic semiconductor composition according to the present inventioncomprises a copolymer composition, the composition having a permittivityat 1000 Hz of greater than 1.5, more preferably greater than 3.4, andyet more preferably between 1.5 and 6.5, even more preferably between 3and 6.5, more preferably between 3.0 to 5.0 and still more preferablybetween 3.4 to 4.5.

The organic semiconductor composition according to the present inventioncan comprise a polycyclic aromatic hydrocarbon copolymer as hereindisclosed. In a preferred embodiment, an organic semiconductorcomposition may comprise a copolymer as defined herein, furthercomprising a polycrystalline polyacene small molecule semiconductor asdescribed in our application WO 2012/164282, wherein the PAHC has apermittivity at 1000 Hz of between 3.4 and 8, preferably between 3.4 and6.5, more preferably between 4 and 6.5, yet more preferably between 3.4to 4.5. In a preferred embodiment, a copolymer as defined herein may beused in combination with a polyacene small molecule or abenzodichalcogenophenobenzodichalcogenophene ‘BXBX’ small molecule,where the ‘dried state’ composition contains between 10 to 50% of thepolyacene small molecule and 10 to 90% of the PAHC.

The organic semiconductor composition according to the present inventioncan comprise a polycyclic aromatic hydrocarbon copolymer as hereindisclosed. In a preferred embodiment, an organic semiconductorcomposition may comprise a copolymer as defined herein, furthercomprising an organic binder, wherein the organic binder has apermittivity at 1000 Hz of between 3.4 and 8, preferably between 3.4 and6.5, more preferably between 4 and 6.5, yet more preferably between 3.4to 4.5.

In a particularly preferred embodiment, a copolymer as defined hereinmay be used in combination with an organic binder, wherein the organicbinder has a permittivity at 1000 Hz of between 3.4 and 8.0, preferablybetween 3.6 and 6.5, more preferably between 3.4 to 4.5.

In yet another preferred embodiment, a copolymer of the inventionpreferably has a permittivity at 1000 Hz of between 3.4 and 8.0,preferably between 3.4 and 4.5.

The concentration of the copolymer and solvent present in thecomposition will vary depending on the preferred solution coatingmethod, for example ink jet printing compositions require low viscosity,low solids loading compositions, whilst screen printing processesrequire high viscosity, high solids loading compositions. Followingdeposition of the copolymer composition, the solvent is preferablyevaporated to afford the semiconductor layer having 1-99.9% by weight ofthe binder and 0.1 to 99% by weight of the copolymer (in the printed ordried state) based on a total weight of the composition; preferably thesemiconductor layer having 25 to 75% by weight of the small moleculepolyacene and 25 to 75% by weight of the copolymer.

In the composition prior to deposition, one or more of theabove-described PAHCs is preferably present at a concentration of atleast 0.1 wt %, preferably 0.5 wt % based on a total weight of thecomposition. The upper limit of the concentration of the PAHC in thecomposition is often near the solubility limit of that copolymer in theparticular solvent at the temperature of the composition during itsapplication to a substrate such as in the fabrication of an electronicdevice. Typical compositions of the present invention comprise one ofthe PAHCs at a concentration ranging from about 0.1 wt %, preferably 0.5wt % to about 20.0 wt % based on a total weight of the composition, moretypically, from about 0.5 wt % to about 10.0 wt %, more typically 0.5 to5.0, more typically 1 to 3 wt %.

In the printed or dried composition, one or more of the above-describedPAHCs is preferably present at a concentration of at least 10 wt % basedon a total weight of the composition, preferably between 10 and 90 wt %,more preferably between 20 and 80 wt %, more preferably between 30 and70 wt %, more preferably between 40 and 60 wt %.

In a preferred embodiment, one or more solvents may be present in theorganic semiconductor compositions.

Suitable solvents include, but are not limited to, tetrahydrofuran,aromatic hydrocarbons such as toluene, o-xylene, m-xylene, p-xylene,mesitylene, bromomesitylene, anisole, bromoanisole, bromobenzene,tetralin, o-xylene, 1,4-dioxane, methylethylketone, gamma-butyrolactone,cyclohexanone, morpholine, N-methylpyrollidone, ethyl acetate, n-butylacetate, dimethylformamide, dimethylacetamide, decalin or mixtures oftwo or more thereof. Preferably, no chlorinated solvents are used.

Solvent blends may also be utilised. Suitable solvent blends include,but are not limited to compositions of the above solvents in conjunctionwith solvents such as dimethylformamide, dimethylacetamide,dimethylsulfoxide, methyl ethyl ketone, dichloromethane,dichlorobenzene, furfuryl alcohol, dimethoxyethane and ethyl acetate,higher boiling point alkanes such as n-heptane and alcohols such asisopropyl alcohol. Such compositions (prior to deposition) preferablycontain a suitable solvent in an amount of greater than 50 wt % based ona total weight of the composition, preferably between 60 and 95 wt %based on a total weight of the composition.

In yet another preferred embodiment, one or more additional compositioncomponents may be present in the organic semiconductor composition.Suitable additional composition components include, but are not limitedto, a polymer additive, a rheological modifier, a surfactant, anothersemiconductor that is a matched hole transfer compound for thecopolymer. In some exemplary embodiments, the compositions comprise apolymer additive selected from the group consisting of polystyrene,poly(alpha-methylstyrene), poly(pentafluorostyrene), poly(methylmethacrylate), poly(4-cyanomethyl styrene), poly(4-vinylphenol), or anyother suitable polymer disclosed in U.S. Patent Application PublicationNo. 2004/0222412 A1 or U.S. Patent Application Publication No.2007/0146426 A1. In some desired embodiments, the polymer additivecomprises polystyrene, poly(alpha-methylstyrene),poly(pentafluorostyrene) or poly(methyl methacrylate). In some exemplaryembodiments, the compositions comprise a surfactant selected fromfluorinated surfactants or fluorosurfactants. When present, eachadditional composition component is independently present in an amountof greater than 0 to about 50 wt % based on a total weight of thecomposition. Preferably, each additional composition component isindependently present in an amount ranging from about 0.0001 to about10.0 wt % based on a total weight of the composition. For example, whena polymer is present in the composition, the polymer additive istypically present in an amount of greater than 0 to about 5.0 wt %,preferably from about 0.5 to about 3.0 wt % based on a total weight ofthe composition. For example, when a surfactant is present in thecomposition, the surfactant is preferably present in an amount ofgreater than 0 to about 1.0 wt %, more typically, from about 0.001 toabout 0.5 wt % based on a total weight of the composition.

The organic semiconductor composition according to the present inventionpreferably has a charge mobility value of at least 0.5 cm²V⁻¹s⁻¹,preferably between 0.5 and 8.0 cm²V⁻¹s⁻¹, more preferably between 0.5and 6.0 cm²V⁻¹s⁻¹, more preferably between 0.8 and 5.0 cm²V⁻¹s⁻¹, morepreferably between 1.0 and 5.0 cm²V⁻¹s⁻¹, more preferably between 1.5and 5.0 cm²V⁻¹s⁻¹, more preferably between 2.0 and 5.0 cm²V⁻¹s⁻¹. Thecharge mobility value of the semiconductor composition can be measuredusing any standard method known to those skilled in the art, such astechniques disclosed in J. Appl. Phys., 1994, Volume 75, page 7954 andWO 2005/055248, preferably by those described in WO 2005/055248.

The organic semiconductor composition according to the present inventionmay be prepared by any known method within the common general knowledgeof a person skilled in the art. In a preferred embodiment, the organicsemiconductor composition is prepared by the method disclosed in WO2005/055248 or by using the method disclosed herein, preferably by usingthe method disclosed herein.

Preferably, organic semiconductor compositions according to the presentinvention are semiconducting compositions having a permittivity at 1000Hz greater than 1.5, more preferably greater than 3.4, and yet morepreferably, between 3.4 and 8. In a preferred embodiment, thecompositions have a permittivity at 1000 Hz of between 4.0 and 7, morepreferably between 4.0 and 6.5, even more preferably between 4.0 and 6and yet more preferably between 3.4 and 4.5.

Organic Semiconductor Layers

The present invention is also concerned with organic semiconductorlayers. In a first aspect of the present invention, the organicsemiconductor layer comprises a PAHC comprising a mixture of at leastone BXBX monomer unit having the Formula (A) and at least one monomerunit having the Formula (B). In a second aspect of the presentinvention, the organic semiconductor layer comprises a PAHC comprising amixture of at least one BXBX monomer unit having the Formula (A) and atleast one monomer unit having the Formula (K). In a third aspect of thepresent invention, the organic semiconductor layer comprises a PAHCcomprising a mixture of at least one BXBX monomer unit having theFormula (A) and at least one monomer unit having the Formula (O).

The organic semiconductor compositions according to the presentinvention may be deposited onto a variety of substrates, to form organicsemiconductor layers.

The organic semiconductor layer according to the present invention maybe prepared using a method comprising the steps of:

(i) Mixing the organic semiconductor composition according to thepresent invention with a solvent to form a semiconductor layerformulation;(ii) Depositing said formulation onto a substrate; and(iii) Optionally removing the solvent to form an organic semiconductorlayer.

Useful substrate materials include, but are not limited to, polymericfilms such as polyamides, polycarbonates, polyimides, polyketones,polyethylene terephthalate (PET) and polyethylene naphthalate (PEN), andinorganic substrates such as silica, alumina, silicon wafers and glass.The surface of a given substrate may be treated, e.g. by reaction ofchemical functionality inherent to the surface with chemical reagentssuch as silanes or exposure of the surface to plasma, in order to alterthe surface characteristics.

Prior to depositing the organic semiconductor composition onto thesubstrate, the composition may be combined with one or more solvents inorder to facilitate the deposition step. Suitable solvents include anysolvent which is able to dissolve both the copolymer, and which uponevaporation from the solution blend, give a coherent, defect-free layer.Suitable solvents for the copolymer can be determined by preparing acontour diagram for the material as described in ASTM Method D 3132 atthe concentration at which the mixture will be employed. The material isadded to a wide variety of solvents as described in the ASTM method.

Suitable solvents include, but are not limited to, tetrahydrofuran,aromatic hydrocarbons such as toluene, o-xylene, m-xylene, p-xylene,mesitylene, bromomesitylene, anisole, bromoanisole, bromobenzene,tetralin, o-xylene, 1,4-dioxane, methylethylketone, gamma-butyrolactone,cyclohexanone, morpholine, N-methylpyrollidone, ethyl acetate, n-butylacetate, dimethylformamide, dimethylacetamide, decalin or mixtures oftwo or more thereof. Preferably, no chlorinated solvents are used.

In accordance with the present invention it has further been found thatthe level of the solids content in the organic semiconducting layerformulation is also a factor in achieving improved mobility values forelectronic devices such as OFETs. The solids content of the formulationis commonly expressed as follows:

${{Solids}\mspace{14mu} {content}\mspace{14mu} (\%)} = {\frac{a + b}{a + b + c} \times 100}$

wherein: a=mass of polyacene small molecule, b=mass of PAHC and c=massof solvent.

The solids content of the formulation is preferably 0.1 to 10% byweight, more preferably 0.5 to 5% by weight.

Suitable conventional deposition methods include, but are not limitedto, spin coating, spray coating, blade/slot-die coating, flexographicprinting, gravure printing, roll-to-roll web-coating, and dip coating,as well as printing processes such as ink-jet printing, screen printing,and offset lithography. In one desired embodiment, the resultingcomposition is a printable composition, even more desirably, an ink jetprintable composition.

Once the composition is deposited onto a substrate surface, the solventmay be removed to form an organic semiconductor layer. Any suitablemethod may be used to remove the solvent. For example, the solvent maybe removed by evaporation or drying. Typically, at least about 80percent of the solvent is removed to form the semiconductor layer. Forexample, at least about 85 weight percent, at least about 90 weightpercent, at least about 92 weight percent, at least about 95 weightpercent, at least about 97 weight percent, at least about 98 weightpercent, at least about 99 weight percent, or at least about 99.5 weightpercent of the solvent is removed.

The solvent often can be evaporated at any suitable temperature. In somemethods, the solvent mixture is evaporated at ambient temperature. Inother methods, the solvent is evaporated at a temperature higher orlower than ambient temperature. For example, a platen supporting thesubstrate can be heated or cooled to a temperature higher or lower thanambient temperature. In still other preferred methods, some or most ofthe solvent can be evaporated at ambient temperature, and any remainingsolvent can be evaporated at a temperature higher than ambienttemperature. In methods where the solvent evaporates at a temperaturehigher than ambient temperature, the evaporation can be carried outunder an inert atmosphere, such as a nitrogen atmosphere.

Alternatively, the solvent can be removed by application of reducedpressure (i.e., at a pressure that is less than atmospheric pressure)such as through the use of a vacuum. During application of reducedpressure, the solvent can be removed at any suitable temperature such asthose described above.

The rate of removal of the solvent can affect the resultingsemiconductor layer. For example, if the removal process is too rapid,poor packing of the semiconductor molecules can occur duringcrystallisation. Poor packing of the semiconductor molecules can bedetrimental to the charge mobility of the semiconductor layer. Thesolvent can evaporate entirely on its own in an uncontrolled fashion(i.e., no time constraints), or the conditions can be controlled inorder to control the rate of evaporation. In order to minimise poorpacking, the solvent can be evaporated while slowing the evaporationrate by covering the deposited layer. Such conditions can lead to asemiconductor layer having a relatively high degree of crystallinity.

After removal of a desired amount of solvent to form the semiconductorlayer, the semiconductor layer can be annealed by exposure to heat orsolvent vapours, i.e., by thermal annealing or solvent annealing.

The organic semiconductor layer according to the present inventionpreferably has a charge mobility value of at least 0.5 cm²V⁻¹s⁻¹,preferably between 0.5 and 8.0 cm²V⁻¹s⁻¹, more preferably between 0.5and 6.0 cm²V⁻¹s⁻¹, more preferably between 0.8 and 5.0 cm²V⁻¹s⁻¹, morepreferably between 1 and 5.0 cm²V⁻¹s⁻¹, more preferably between 1.5 and5.0 cm²V⁻¹s⁻¹, more preferably between 2.0 and 5.0 cm²V⁻¹s⁻¹. The chargemobility value of the semiconductor layer can be measured using anystandard method known to those skilled in the art, such as techniquesdisclosed in J. Appl. Phys., 1994, Volume 75, page 7954 and WO2005/055248, preferably by those described in WO 2005/055248.

Preferably, the organic semiconductor layer(s) of the present inventionare semiconducting layers having a permittivity at 1000 Hz of between3.4 and 8. In a preferred embodiment, the layer(s) have a permittivityat 1000 Hz of between 4.0 and 7, more preferably between 4.0 and 6.5,yet more preferably between 4.0 and 6 and even more preferably between3.4 and 4.5

Electronic Devices

The invention additionally provides an electronic device comprising theorganic semiconductor composition according to the present invention. Ina first aspect of the present invention, the electronic device maycomprise an organic semiconductor composition comprising a PAHCcomprising a mixture of at least one BXBX monomer unit having theFormula (A) and at least one monomer unit having the Formula (B). In asecond aspect of the present invention, the electronic device maycomprise an organic semiconductor composition comprising a PAHCcomprising a mixture of at least one BXBX monomer unit having theFormula (A) and at least one monomer unit having the Formula (K). In athird aspect of the present invention, the electronic device maycomprise an organic semiconductor composition comprising a PAHCcomprising a mixture of at least one BXBX monomer unit having theFormula (A) and at least one monomer unit having the Formula (O).

The composition may be used, for example, in the form of asemiconducting layer or film. Additionally, the invention preferablyprovides an electronic device comprising the organic semiconductor layeraccording to the present invention.

The thickness of the layer or film may be between 0.02 and 20 microns,0.2 and 20 microns, preferably between 0.05 and 10 microns, preferablybetween 0.5 and 10 microns, between 0.05 and 5 microns, even morepreferably between 0.5 and 5 microns, yet more preferably between 0.5and 2 microns, and more preferably between 0.02 and 1 microns.

The electronic device may include, without limitation, organic fieldeffect transistors (OFETS), organic light emitting diodes (OLEDS),photodetectors, organic photovoltaic (OPV) cells, sensors, lasers,memory elements and logic circuits.

Exemplary electronic devices of the present invention may be fabricatedby solution deposition of the above-described organic semiconductorcomposition onto a substrate.

DETAILED DESCRIPTION OF THE INVENTION General

For the heteroacene monomers used in the invention whilst one isomer isshown the invention applies to pure cis isomer, pure trans isomer andmixtures of cis and trans isomers.

The term “about” in relation to a numerical value x means, for example,x ±10%.

The word “substantially” does not exclude “completely” e.g. acomposition which is “substantially free” from Y may be completely freefrom Y. Where necessary, the word “substantially” may be omitted fromthe definition of the invention.

“Molecular weight” of a polymeric material (including monomeric ormacromeric materials), as used herein, refers to the number-averagemolecular weight unless otherwise specifically noted or unless testingconditions indicate otherwise.

A “polymer” means a material formed by polymerising and/or crosslinkingone or more monomers, macromers and/or oligomers and having two or morerepeat units.

As used herein, the term “alkyl” group refers to a straight or branchedsaturated monovalent hydrocarbon radical, having the number of carbonatoms as indicated. By way of non limiting example, suitable alkylgroups include, methyl, ethyl, propyl, n-butyl, t-butyl, iso-butyl anddodecanyl.

As used herein, the term “alkoxy” group include without limitation,methoxy, ethoxy, 2-methoxyethoxy, t-butoxy, etc.

As used herein, the term “amino” group includes, without limitation,dimethylamino, methylamino, methylphenylamino, phenylamino, etc.

The term “carbyl” refers to any monovalent or multivalent organicradical moiety which comprises at least one carbon atom other withoutany non-carbon atoms (—C≡C), or optionally combined with at least onenon-carbon atoms such as N, O, S, P, SI, Se, As, Te or Ge (for examplecarbonyl etc.).

The term “hydrocarbon” group denotes a carbyl group that additionallycontains one or more H atoms and optionally contains one or more heteroatoms.

A carbyl or hydrocarbyl group comprising 3 or more carbon atoms may belinear, branched and/or cyclic, including spiro and/or fused rings.

Preferred carbyl or hydrocarbyl groups include alkyl, alkoxy,alkylcarbonyl, alkylcarbonyloxy, alkoxycarbonyloxy, each of which isoptionally substituted and has 1 to 40, preferably 1 to 18 carbon atoms,furthermore optionally substituted aryl, aryl derivative or aryloxyhaving 6 to 40, preferably 6 to 18 carbon atoms, furthermorealkylaryloxy, arylcarbonyl, aryloxycarbonyl, arylcarbonyloxy andaryloxycarbonyloxy, each or which is optionally substituted and has 7 to40, more preferable 7 to 25 carbon atoms.

The carbyl or hydrocarbyl group may be saturated or unsaturated acyclicgroup, or a saturated or unsaturated cyclic group. Unsaturated acyclicor cyclic groups are preferred, especially alkenyl and alkynyl groups(especially ethynyl).

In the polyacenes of the present invention, the optional substituents onthe said C₁-C₄₀ carbyl or hydrocarbyl groups for R₁-R₁₄ etc. preferablyare selected from: silyl, sulpho, sulphonyl, formyl, amino, imino,nitrilo, mercapto, cyano, nitro, halo, C₁₋₄ alkyl, C₆₋₁₂ aryl, C₁₋₄alkoxy, hydroxy and/or all chemically possible combinations thereof.More preferable among these optional substituents are silyl and C₆₋₁₂aryl and most preferable is silyl.

“Substituted alkyl group” refers to an alkyl group having one or moresubstituents thereon, wherein each of the one or more substituentscomprises a monovalent moiety containing one or more atoms other thancarbon and hydrogen either alone (e.g., a halogen such as F) or incombination with carbon (e.g., a cyano group) and/or hydrogen atoms(e.g., a hydroxyl group or a carboxylic acid group).

“Alkenyl group” refers to a monovalent group that is a radical of analkene, which is a hydrocarbon with at least one carbon-carbon doublebond. The alkenyl can be linear, branched, cyclic, or combinationsthereof and typically contains 2 to 30 carbon atoms. In someembodiments, the alkenyl contains 2 to 20, 2 to 14, 2 to 10, 4 to 10, 4to 8, 2 to 8, 2 to 6, or 2 to 4 carbon atoms. Exemplary alkenyl groupsinclude, but are not limited to, ethenyl, propenyl, and butenyl.

“Substituted alkenyl group” refers to an alkenyl group having (i) one ormore C—C double bonds, and (ii) one or more substituents thereon,wherein each of the one or more substituents comprises a monovalentmoiety containing one or more atoms other than carbon and hydrogeneither alone (e.g., a halogen such as F) or in combination with carbon(e.g., a cyano group) and/or hydrogen atoms (e.g., a hydroxyl group or acarboxylic acid group).

“Alkynyl group” refers to a monovalent group that is a radical of analkyne, a hydrocarbon with at least one carbon-carbon triple bond. Thealkynyl can be linear, branched, cyclic, or combinations thereof andtypically contains 2 to 30 carbon atoms. In some embodiments, thealkynyl contains 2 to 20, 2 to 14, 2 to 10, 4 to 10, 4 to 8, 2 to 8, 2to 6, or 2 to 4 carbon atoms. Exemplary alkynyl groups include, but arenot limited to, ethynyl, propynyl, and butynyl.

“Substituted alkynyl group” refers to an alkynyl group having (i) one ormore C—C triple bonds, and (ii) one or more substituents thereon,wherein each of the one or more substituents comprises a monovalentmoiety containing one or more atoms other than carbon and hydrogeneither alone (e.g., a halogen such as F) or in combination with carbon(e.g., a cyano group) and/or hydrogen atoms (e.g., a hydroxyl group or acarboxylic acid group or a silyl group).

“Cycloalkyl group” refers to a monovalent group that is a radical of aring structure consisting of 3 or more carbon atoms in the ringstructure (i.e., only carbon atoms in the ring structure and one of thecarbon atoms of the ring structure is the radical).

“Substituted cycloalkyl group” refers to a cycloalkyl group having oneor more substituents thereon, wherein each of the one or moresubstituents comprises a monovalent moiety containing one or more atoms(e.g., a halogen such as F, an alkyl group, a cyano group, a hydroxylgroup, or a carboxylic acid group).

“Cycloalkylalkylene group” refers to a monovalent group that is a ringstructure consisting of 3 or more carbon atoms in the ring structure(i.e., only carbon atoms in the ring), wherein the ring structure isattached to an acyclic alkyl group (typically, from 1 to 3 carbon atoms,more typically, 1 carbon atom) and one of the carbon atoms of theacyclic alkyl group is the radical. “Substituted cycloalkylalkylenegroup” refers to a cycloalkylalkylene group having one or moresubstituents thereon, wherein each of the one or more substituentscomprises a monovalent moiety containing one or more atoms (e.g., ahalogen such as F, an alkyl group, a cyano group, a hydroxyl group, or acarboxylic acid group).

“Aryl group” refers to a monovalent group that is a radical of anaromatic carbocyclic compound. The aryl can have one aromatic ring orcan include up to 5 carbocyclic ring structures that are connected to orfused to the aromatic ring. The other ring structures can be aromatic,non-aromatic, or combinations thereof. Examples of preferred aryl groupsinclude, but are not limited to, phenyl, 2-tolyl, 3-tolyl, 4-tolyl,biphenyl, 4-phenoxyphenyl, 4-fluorophenyl, 3-carbomethoxyphenyl,4-carbomethoxyphenyl, terphenyl, anthryl, naphthyl, acenaphthyl,anthraquinonyl, phenanthryl, anthracenyl, pyrenyl, perylenyl, andfluorenyl.

“Substituted aryl group” refers to an aryl group having one or moresubstituents on the ring structure, wherein each of the one or moresubstituents comprises a monovalent moiety containing one or more atoms(e.g., a halogen such as F, an alkyl group, a cyano group, a hydroxylgroup, or a carboxylic acid group).

“Arylalkylene group” refers to a monovalent group that is an aromaticring structure consisting of 6 to 10 carbon atoms in the ring structure(i.e., only carbon atoms in the ring structure), wherein the aromaticring structure is attached to an acyclic alkyl group having one or morecarbon atoms (typically, from 1 to 3 carbon atoms, more typically, 1carbon atom) and one of the carbons of the acyclic alkyl group is theradical.

“Substituted arylalkylene group” refers to an arylalkylene group havingone or more substituents thereon, wherein each of the one or moresubstituents comprises a monovalent moiety containing one or more atoms(e.g., a halogen such as F, an alkyl group, a cyano group, a hydroxylgroup, or a carboxylic acid group).

“Acetyl group” refers to a monovalent radical having the formula—C(O)CH₃.

“Heterocyclic ring” refers to a saturated, partially saturated, orunsaturated ring structure comprising at least one of O, N, S and Se inthe ring structure.

“Substituted heterocyclic ring” refers to a heterocyclic ring having oneor more substituents bonded to one or more members of the ringstructure, wherein each of the one or more substituents comprises amonovalent moiety containing one or more atoms (e.g., a halogen such asF, an alkyl group, a cyano group, a hydroxyl group, or a carboxylic acidgroup).

“Carbocyclic ring” refers to a saturated, partially saturated, orunsaturated ring structure comprising only carbon in the ring structure.

“Substituted carbocyclic ring” refers to a carbocyclic ring having oneor more substituents bonded to one or more members of the ringstructure, wherein each of the one or more substituents comprises amonovalent moiety containing one or more atoms (e.g., a halogen such asF, an alkyl group, a cyano group, a hydroxyl group, or a carboxylic acidgroup).

“Ether group” refers to a —R_(a)—O—R_(b) radical wherein R_(a) is abranched or unbranched alkylene, arylene, alkylarylene or arylalkylenehydrocarbon and R_(b) is a branched or unbranched alkyl, aryl, alkylarylor arylalkyl hydrocarbon.

“Substituted ether group” refers to an ether group having one or moresubstituents thereon, wherein each of the one or more substituentscomprises a monovalent moiety containing one or more atoms other thancarbon and hydrogen either alone (e.g., a halogen such as F) or incombination with carbon (e.g., a cyano group) and/or hydrogen atoms(e.g., a hydroxyl group or a carboxylic acid group).

Unless otherwise defined, a “substituent” or “optional substituent” ispreferably selected from the group consisting of halo (I, Br, Cl, F),CN, NO₂, NH₂, —COOH and OH.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a representation of top contact/bottom gate organic thin filmtransistor (OTFT)

FIG. 2 is a representation of bottom contact/bottom gate (OTFT)

FIG. 3 is a representation of top contact/top gate (OTFT)

FIG. 4 is a representation of bottom contact/top gate (OTFT)

Labels—A: Substrate; B: Gate electrode; C: Dielectric layer; D:Semiconductor layer; E: Source electrode; F: Gate electrode

EXAMPLES OF THE PRESENT INVENTION

The following examples of the present invention are merely exemplary andshould not be viewed as limiting the scope of the invention.

Measurement of the Capacitance of the Polymer Binder

The polymer binder was diluted with tetralin in order to lower itsviscosity and make it possible to obtain a film thickness of ˜1 micronwhen spin coated for the spin speed range 1000-2000 rpm/s. The polymerbinder solution was spin coated at 500 rpm for 10 seconds, followed by1500 rpm for 30 seconds, onto ITO coated and cleaned 1×1 inch glasssubstrates.

To clean the ITO coated substrates they were submerged in a 3% solutionof DECon 90 and put in an ultrasonic bath (water temperature >65° C.),washed with deionised water, submerged in deionised water and put in anultrasonic bath (water temperature >65° C.), washed a further time withdeionised water, submerged in isopropyl alcohol and then put in anultrasonic bath (water temperature >65° C.), and then spin dried.

After deposition of the polymer binder the substrate was annealed on ahotplate at 120° C. for 5 minutes.

The substrate was then covered with a capacitance shadow mask, and topelectrodes were deposited by evaporation of gold using a thermaldeposition method. In order to determine the exact thickness of thepolymer binder layer, the thickness was measured using a Dektak 3030profilometer (available from Veeco, Plainview N.Y.) at three differentpositions and averaged; these values were subsequently used to calculatethe dielectric constants of the polymer binders.

Capacitance measurements were then carried out using impedance analyserAgilent 43961A and a probe station. In order to improve the electricalcontact between the ITO back electrode and the external probe electrode,a conductive silver paste was applied. The sample being measured wasplaced in a metal box on the metal plate to ensure minimum influencefrom the external environment.

Before each set of measurements was obtained, the analyser wascalibrated using the 43961A Impedance Test Kit as a compensation routinewas carried out to account for internal capacitance of the analyser andtest fixture. The measurement calibration was carried out with open andshorted circuit; the dielectric constant was calculated using thefollowing equation:

C=ε×ε _(o)×(A/d).

Wherein C is the capacitance (Farads), A is the area (m²), d is thecoating thickness (m), ε is the dielectric constant (permittivity), andε_(o) is the permittivity of free space and is taken as 8.8854×10⁻¹²F/m.

As a reference sample, a polystyrene sample (Mw˜350,000) having athickness of 1 μm was tested. The measured and calculated dielectricconstant of the polystyrene reference was ε=2.55 at 10,000 Hz, which isin good agreement with the reported value (ε˜2.5), refer to J. R.Wunsch, Polystyrene-Synthesis, Production and Applications, Rapra ReviewReports, 2000, Volume 10, No. 4, page 32.

OTFT Fabrication Method

A substrate (either glass or a polymer substrate such as PEN) ispatterned with Au source drain electrodes either by a process of thermalevaporation through a shadow mask or by photolithography (an adhesionlayer of either Cr or Ti is deposited on the substrate prior todeposition of Au). The Au electrodes can the optionally be cleaned usingan O₂ plasma cleaning process. A solution of organic semiconductor inbinder is then applied by spin coating (the sample is flooded with thesolution and the substrate is then spun at 500 rpm for 5 seconds then1500 rpm for 1 minute). The coated substrate is then dried in air on ahot stage. The dielectric material, for example 3 wt % PTFE-AF 1600(Sigma-Aldrich cat #469610) dissolved in FC-43) was then applied to thesubstrate by spin coating (sample flooded then spun at 500 rpm for 5seconds then 1500 rpm for 30 seconds). The substrate was then dried inair on a hot stage (100° C. for 1 minute). A gate electrode (Au) is thendefined over the channel area by evaporation through a shadow mask.

The mobility of the OTFT for the binders is characterised by placing ona manual probe station connected to a Keithley SCS 4200 semiconductoranalyzer. The source drain voltage (V_(DS)) is set at −2V (linear) or−40V (saturation) and the gate voltage (V_(G)) scanned from +20V to−60V. Drain current is measured and mobility calculated from thetransconductance.

The mobility of the OTFT for the formulations is characterised byplacing on a semi-auto probe station connected to a Keithley SCS 4200semiconductor analyzer. The source drain voltage is set at −2V and thegate voltage scanned from +20V to −40V. Drain current is measured andmobility calculated from the transconductance.

In linear regime, when |V_(G)|>|V_(DS)|, the source-drain current varieslinearly with V_(G). Thus the field effect mobility (μ) can becalculated from the gradient (S) of I_(DS) vs. V_(G) given by equation 1(where C_(i) is the capacitance per unit area, W is the channel widthand L is the channel length):

$\begin{matrix}{\mspace{340mu} {{S = \frac{\text{?}}{L}}{\text{?}\text{indicates text missing or illegible when filed}}}} & {{Equation}\mspace{14mu} 1}\end{matrix}$

In the saturation regime, the mobility is determined by finding theslope of IDs^(1/2) vs. V_(G) and solving for the mobility (Equation 2)

$\begin{matrix}{\mspace{335mu} {{I\text{?}\frac{\text{?}}{\text{?}}}{\text{?}\text{indicates text missing or illegible when filed}}}} & {{Equation}\mspace{14mu} 2}\end{matrix}$

Examples of the Present Invention

The following examples are intended to explain the invention withoutrestricting it. The methods, structures and properties described hereincan also be applied to materials that are claimed in this invention butnot explicitly described in the examples.

Particularly preferred PAHCs according to the present invention areshown in the following tables 1 to 3:

TABLE 1 Preferred PAHCs

Case 1 Y¹ = Y² are S R^(′a), R^(′b), R^(′c), R^(′d), R^(′e) = H R¹, R²,R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R⁴ and R¹⁰ are C₁ to C₁₄ alkylgroups, most preferably n-octyl groups. R³ and, R⁹ are bonds to anotherunit of Monomer (A) or (B). Case 2 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸,R¹¹, R¹² are all H. R³ and R⁹ are C₁ to C₁₄ alkyl groups, mostpreferably n-octyl groups. R⁴ and R¹⁰ are bonds to another unit ofMonomer (A) or (B). Case 3 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹,R¹² are all H. R⁴ and R¹⁰ are CF₃ groups. R³ and R⁹ are bonds to anotherunit of Monomer (A) or (B). Case 4 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸,R¹¹, R¹² are all H. R³ and, R⁹ are CF₃ groups. R⁴ and R¹⁰ are bonds toanother unit of Monomer (A) or (B). Case 1 R^(′b), R^(′d), R^(′e) = HCase 2 R^(′a) and R^(′c) = C₁ to C₄ Case 3 alkyl Case 4 Case 1 R^(′b),R^(′c), R^(′d), R^(′e) = H Case 2 R^(′a) = C₁ to C₆ alkoxy Case 3 (i)R^(′a) = methoxy Case 4 (ii) R^(′a) = ethoxy Case 1 R^(′a), R^(′b),R^(′d), R^(′e) = H Case 2 R^(′c) = C₁ to C₆ alkoxy Case 3 (i) R^(′c) =methoxy Case 4 (ii) R^(′c) = ethoxy Case 1 R^(′a), R^(′b), R^(′c),R^(′d) = H Case 2 R^(′e) = C₁ to C₆ alkoxy Case 3 (i) R^(′e) = methoxyCase 4 (ii) R^(′e) = ethoxy Case 1 R^(′b), R^(′d), R^(′e) = H Case 2R^(′a) = R^(′c) = C₁ to C₆ alkoxy Case 3 (i) R^(′a) = R^(′c) = methoxyCase 4 (ii) R^(′a) = R^(′c) = ethoxy Case 1 R^(′b), R^(′d) = H Case 2R^(′a), R^(′c), R^(′e) = C₁ to C₆ Case 3 alkoxy Case 4 (i) R^(′a),R^(′c), R^(′e) = methoxy (ii) R^(′a), R^(′c), R^(′e) = ethoxy Case 1R^(′b), R^(′d) = H Case 2 R^(′b), R^(′c), R^(′d) = C₁ to C₆ Case 3alkoxy Case 4 (i) R^(′b), R^(′c), R^(′d) = methoxy (ii) R^(′b), R^(′c),R^(′d) = ethoxy Case 1 R^(′b), R^(′c), R^(′d), R^(′e) = H Case 2 R^(′a)= Cyano (CN) Case 3 Case 4 Case 1 R^(′b), R^(′c), R^(′d), R^(′e) = HCase 2 R^(′a) = Isopropylcyano Case 3 group Case 4 Monomer B:  

Case 1 R^(′a), R^(′b), R^(′d), R^(′e) = H Case 2 R^(′c) = IsopropylcyanoCase 3 group Case 4 Monomer B:  

TABLE 2 Preferred PAHCs

Case 1 Y¹ = Y² are S R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, preferablyn-octyl R^(′a), R^(′b), R^(′c), R^(′d), R^(′e) = H R¹, R², R⁵, R⁶, R⁷,R⁸, R¹¹, R¹² are all H. groups R⁴ and R¹⁰ are C₁ to C₁₄ alkyl groups,R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or C₁ to C₄ most preferablyn-octyl groups. alkoxy groups; or cyano groups; or isopropyl R³ and, R⁹are bonds to another unit of Monomer cyano groups. (A) or (B). Case 2 Y¹= Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R³ and R⁹ are C₁to C₁₄ alkyl groups, most preferably n-octyl groups. R⁴ and R¹⁰ arebonds to another unit of Monomer (A) or (B). Case 3 Y¹ = Y² are S R¹,R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R⁴ and R¹⁰ are CF₃ groups. R³and R⁹ are bonds to another unit of Monomer (A) or (B). Case 4 Y¹ = Y²are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹, R¹² are all H. R³ and, R⁹ are CF₃groups. R⁴ and R¹⁰ are bonds to another unit of Monomer (A) or (B). Case1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octyl R^(′b),R^(′d), R^(′e) = H Case 2 groups R^(′a) and R^(′c) = C₁ to Case 3R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or C₁ to C₄ C₄ alkyl Case 4alkoxy groups; or cyano groups; or isopropyl cyano groups. Case 1 R^(1′)= R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octyl R^(′b), R^(′c),R^(′d), R^(′e) = H Case 2 groups R^('a) = C₁ to C₆ Case 3 R^(3′), R^(4′)= H or C₁ to C₄ alkyl groups; or C₁ to C₄ alkoxy Case 4 alkoxy groups;or cyano groups; or isopropyl (i) R^(′a) = methoxy cyano groups. (ii)R^(′a) = ethoxy Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group,preferably n-octyl R^(′a), R^(′b), R^(′d), R^(′e) = H Case 2 groupsR^(′c) = C₁ to C₆ Case 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; orC₁ to C₄ alkoxy Case 4 alkoxy groups; or cyano groups; or isopropyl (i)R^(′c) = methoxy cyano groups. (ii) R^(′c) = ethoxy Case 1 R^(1′) =R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octyl R^(′a), R^(′b),R^(′c), R^(′d) = H Case 2 groups R^(e′) = C₁ to C₆ Case 3 R^(3′), R^(4′)= H or C₁ to C₄ alkyl groups; or C₁ to C₄ alkoxy Case 4 alkoxy groups;or cyano groups; or isopropyl (i) R^(′e) = methoxy cyano groups. (ii)R^(′e) = ethoxy Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group,preferably n-octyl R^(′b), R^(′d), R^(′e) = H Case 2 groups R^(′a) =R^(′c) = C₁ to C₆ Case 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; orC₁ to C₄ alkoxy Case 4 alkoxy groups; or cyano groups; or isopropyl (i)R^(′a) = R^(′c) = methoxy cyano groups. (ii) R^(′a) = R^(′c) = ethoxyCase 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octylR^(′b), R^(′d) = H Case 2 groups R^(′a), R^(′c), R^(′e) = C₁ to Case 3R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or C₁ to C₄ C₆ alkoxy Case4 alkoxy groups; or cyano groups; or isopropyl (i) R^(′a), R^(′c),R^(′e) = methoxy cyano groups. (ii) R^(′a), R^(′c), R^(′e) = ethoxy Case1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octyl R^(′b),R^(′d) = H Case 2 groups R^(′b), R^(′c), R^(′d) = C₁ to Case 3 R^(3′),R^(4′) = H or C₁ to C₄ alkyl groups; or C₁ to C₄ C₆ alkoxy Case 4 alkoxygroups; or cyano groups; or isopropyl (i) R^(′b), R^(′c), R^(′d) =methoxy cyano groups. (ii) R^(′b), R^(′c), R^(′d) = ethoxy Case 1 R^(1′)= R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octyl R^(′b), R^(′c),R^(′d), R^(′e) = H Case 2 groups R^(′a) = Cyano (CN) Case 3 R^(3′),R^(4′) = H or C₁ to C₄ alkyl groups; or C₁ to C₄ Case 4 alkoxy groups;or cyano groups; or isopropyl cyano groups. Case 1 R^(1′) = R^(2′) = C₁to C₁₄ alkyl group, preferably n-octyl R^(′b), R^(′c), R^(′d), R^(′e) =H Case 2 groups R^(′a) = Isopropylcyano Case 3 R^(3′), R^(4′) = H or C₁to C₄ alkyl groups; or C₁ to C₄ group Case 4 alkoxy groups; or cyanogroups; or isopropyl cyano groups. Monomer C:  

Case 1 R^(1′) = R^(2′) = C₁ to C₁₄ alkyl group, preferably n-octylR^(′a), R^(′b), R^(′d), R^(′e) = H Case 2 groups R^(′c) = lsopropylcyanoCase 3 R^(3′), R^(4′) = H or C₁ to C₄ alkyl groups; or C₁ to C₄ groupCase 4 alkoxy groups; or cyano groups; or isopropyl cyano groups.Monomer C:  

TABLE 3 Preferred PAHCs

Case 1 Y¹ = Y² are S R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄alkyl group, R^(′a), R^(′b), R^(′c), R^(′d), R^(′e) = H R¹, R², R⁵, R⁶,R⁷, R⁸, R¹¹, R¹² are all H. preferably n-octyl groups R⁴ and R¹⁰ are C₁to C₁₄ alkyl groups, most preferably n-octyl R^(5′), R^(6′) and R^(7′)are H or C₁ to C₄ alkyl groups; or C₁ groups. to C₄ alkoxy groups; orcyano groups; or R³ and, R⁹ are bonds to another unit of Monomerisopropyl cyano groups. (A) or (B). Case 2 Y¹ = Y² are S R¹, R², R⁵, R⁶,R⁷, R⁸, R¹¹, R¹² are all H. R³ and R⁹ are C₁ to C₁₄ alkyl groups, mostpreferably n-octyl groups. R⁴ and R¹⁰ are bonds to another unit ofMonomer (A) or (B). Case 3 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸, R¹¹,R¹² are all H. R⁴ and R¹⁰ are CF₃ groups. R³ and R⁹ are bonds to anotherunit of Monomer (A) or (B). Case 4 Y¹ = Y² are S R¹, R², R⁵, R⁶, R⁷, R⁸,R¹¹, R¹² are all H. R³ and, R⁹ are CF₃ groups. R⁴ and R¹⁰ are bonds toanother unit of Monomer (A) or (B). Case 1 R^(1′), R^(2′), R^(3′) andR^(4′) are C₁ to C₁₄ alkyl group, R^(′b), R^(′d), R^(′e) = H Case 2preferably n-octyl groups R^(′a) and R^(′c) = C₁ to Case 3 R^(5′),R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups; or C₁ C₄ alkyl Case 4to C₄ alkoxy groups; or cyano groups; or isopropyl cyano groups. Case 1R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′b),R^(′c), R^(′d), R^(′e) = H Case 2 preferably n-octyl groups R^(′a) = C₁to C₆ Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups;or C₁ alkoxy Case 4 to C₄ alkoxy groups; or cyano groups; or (i) R^(′a)= methoxy isopropyl cyano groups. (ii) R^(′a) = ethoxy Case 1 R^(1′),R^(2′), R^(3′) and R^(4′) are C₁t o C₁₄ alkyl group, R^(′a), R^(′b),R^(′d), R^(′e) = H Case 2 preferably n-octyl groups R^(′c) = C₁ to C₆Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups; or C₁alkoxy Case 4 to C₄ alkoxy groups; or cyano groups; or (i) R^(′c) =methoxy isopropyl cyano groups. (ii) R^(′c) = ethoxy Case 1 R^(1′),R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′a), R^(′b),R^(′c), R^(′d) = H Case 2 preferably n-octyl groups R^(′e) = C₁ to C₆Case 3 alkoxy Case 4 (i) R^(′e) = methoxy (ii) R^(′e) = ethoxy Case 1R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′b),R^(′d), R^(′e) = H Case 2 preferably n-octyl groups R^(′a) = R^(′c) = C₁to C₆ Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ to C₄ alkyl groups;or C₁ alkoxy Case 4 to C₄ alkoxy groups; or cyano groups; or (i) R^(′a)= R^(′c) = methoxy isopropyl cyano groups. (ii) R^(′a) = R^(′c) = ethoxyCase 1 R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group,R^(′b), R^(′d) = H Case 2 preferably n-octyl groups R^(′a), R^(′c),R^(′e) = C₁ to Case 3 R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄alkyl group, C₆ alkoxy Case 4 preferably n-octyl groups (i) R^(′a),R^(′c), R^(′e) = methoxy (ii) R^(′a), R^(′c), R^(′e) = ethoxy Case 1R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group, R^(′a),R^(′e) = H Case 2 preferably n-octyl groups R^(′b), R^(′c), R^(′d) = C₁to Case 3 C₆ alkoxy Case 4 (i) R^(′b), R^(′c), R^(′d) = methoxy (ii)R^(′b), R^(′c), R^(′d) = ethoxy Case 1 R^(′b), R^(′c), R^(′d), R^(′e) =H Case 2 R^(′a) = Cyano (CN) Case 3 Case 4 Case 1 R^(1′), R^(2′), R^(3′)and R^(4′) are C₁ to C₁₄ alkyl group, R^(′b), R^(′c), R^(′d), R^(′e) = HCase 2 preferably n-octyl groups R^(′a) = Isopropylcyano Case 3 groupCase 4 Monomer C:  

Case 1 R^(1′), R^(2′), R^(3′) and R^(4′) are C₁ to C₁₄ alkyl group,R^(′a), R^(′b), R^(′d), R^(′e) = H Case 2 preferably n-octyl groupsR^(′c) = Isopropylcyano Case 3 R^(5′), R^(6′) and R^(7′) are H or C₁ toC₄ alkyl groups; or C₁ group Case 4 to C₄ alkoxy groups; or cyanogroups; or isopropyl cyano groups. Monomer C:  

The organic semiconductors compounds specified in the table areparticularly preferred as they combine the beneficial properties of highcharge transport mobility (of the binders) with a polarity that is morecompatible with benign, non-chlorinated solvents that will be desirablefor use in large area printing. In addition, as these compounds are morepolar once deposited as the OSC layer, or alternatively as a componentin the OSC layer, they are expected to be resistant to beingre-dissolved by the hydrophobic solvents used for the organic gateinsulators (OGI) such as Cytop. Furthermore, it is expected that thepolar binders are useful for both top gate and bottom gate OTFTs,particularly for bottom gate OTFTs.

1. A Polycyclic Aromatic Hydrocarbon Copolymer (PAHC) comprising amixture of at least one BXBX monomer unit having the Formula (A) and atleast one monomer unit having the Formula (B):

wherein Y¹ and Y² are independently S or Se; k and l are independently 0or 1 wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ andR¹², which may be the same or different, independently representshydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; a C₂-C₁₀ alkynyl groupsubstituted with a SiH₂R²² group, a C₂-C₁₀ alkynyl substituted with aSiHR²²R²³ group, or a C₂-C₁₀ alkynyl substituted with a—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group; wherein each R²² group isindependently selected from the group consisting of a branched orunbranched, substituted or unsubstituted C₁-C₁₀ alkyl group, a branchedor unbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₂-C₁₀ alkenyl group, and a substituted or unsubstitutedC₆-C₂₀ cycloalkylalkylene group; each R²³ group is independentlyselected from the group consisting of a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₁₀ alkenyl group, a substituted orunsubstituted C₂-C₂₀ cycloalkyl group, and a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group; R²⁴ is independentlyselected from the group consisting of hydrogen, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group, a substituted C₅-C₂₀ arylgroup, a substituted or unsubstituted C₆-C₂₀ arylalkylene group, anacetyl group, a substituted or unsubstituted C₃-C₂₀ heterocyclic ringcomprising at least one of O, N, S and Se in the ring; wherein x=1 or 2;y=1 or 2; z=0 or 1; and (x+y+z)=3; wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹and R²⁰ independently represent H or optionally substituted C₁-C₄₀carbyl or hydrocarbyl group optionally comprising one or moreheteroatoms; wherein R¹⁷ represents a halogen atom, H or optionallysubstituted C₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionallycomprising one or more heteroatoms; wherein k and l are independently 0or 1; wherein at least two of R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, and R¹², area bond, represented by

*, to another monomer unit having the Formula (A) or (B); and whereinAr₁, Ar₂ and Ar₃, which may be the same or different, each represent,independently if in different repeat units, an optionally substitutedC₆₋₄₀ aromatic group (mononuclear or polynuclear), wherein preferably atleast one of Ar₁, Ar₂ and Ar₃ is substituted with at least one polar orpolarising groups; and wherein the copolymer is a random copolymer.
 2. APAHC according to claim 1, comprising at least 20 to 40% of monomer (A)and at least 60 to 80% of monomer (B), based on the total of all monomerunits (A) and (B) in the copolymer.
 3. A PAHC according to claim 1,wherein monomer unit (B) having the, Ar₁, Ar₂ and Ar₃, which may be thesame or different, each representing, independently if in differentrepeat units, an optionally substituted C₆₋₂₀ aromatic group(mononuclear or polynuclear), wherein at least one of Ar₁, Ar₂ and Ar₃is substituted with at least one or more polar or polarising group, andn=1 to
 20. 4. A PAHC according to claim 3, wherein Ar₁, Ar₂ and Ar₃ areall phenyl which may be independently substituted with 1 or 2 groupsselected from methoxy, cyanomethyl, CN and mixtures thereof, and n=1 to10.
 5. A PAHC according to claim 1, further comprising one or moremonomers (C), (D), (D′) and/or (E):

wherein each R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′),each of which may be the same or different, is selected from the samegroup as R¹, R², R³, R⁴, R⁵, R⁶ and R⁷, as defined in claim 1; whereinn′=1 to 3; and wherein monomer (A) is present in an amount of at least20 wt. %; monomer (B) is present in an amount of at least 60 wt. % andthe remainder is comprised of monomers (C), (D), (D′) and/or (E), basedon the total weight of all monomer units in the copolymer.
 6. APolycyclic Aromatic Hydrocarbon Copolymer (PAHC) comprising a mixture ofat least one BXBX monomer unit having the Formula (A) and at least onemonomer unit having the Formula (K):

wherein Y¹ and Y² are independently S or Se; k and l are independently 0or 1 wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ andR¹²; which may be the same or different, independently representshydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; a C₂-C₁₀ alkynyl groupsubstituted with a SiH₂R²² group, a C₂-C₁₀ alkynyl substituted with aSiHR²²R²³ group, or a C₂-C₁₀ alkynyl substituted with a—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group; wherein each R²² group isindependently selected from the group consisting of a branched orunbranched, substituted or unsubstituted C₁-C₁₀ alkyl group, a branchedor unbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₂-C₁₀ alkenyl group, and a substituted or unsubstitutedC₆-C₂₀ cycloalkylalkylene group; each R²³ group is independentlyselected from the group consisting of a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₁₀ alkenyl group, a substituted orunsubstituted C₂-C₂₀ cycloalkyl group, and a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group; R²⁴ is independentlyselected from the group consisting of hydrogen, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group, a substituted C₅-C₂₀ arylgroup, a substituted or unsubstituted C₆-C₂₀ arylalkylene group, anacetyl group, a substituted or unsubstituted C₃-C₂₀ heterocyclic ringcomprising at least one of O, N, S and Se in the ring; wherein x=1 or 2;y=1 or 2; z=0 or 1; and (x+y+z)=3; wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹and R²⁰ independently represent H or optionally substituted C₁-C₄₀carbyl or hydrocarbyl group optionally comprising one or moreheteroatoms; wherein R¹⁷ represents a halogen atom, H or optionallysubstituted C₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionallycomprising one or more heteroatoms; wherein k and l are independently 0or 1; wherein at least two of R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, and R¹², area bond, represented by

*, to another monomer unit having the Formula (A) or (K); and whereineach R^(1′), R^(2′), R^(3′) and R^(4′), each of which may be the same ordifferent, is selected from the same group as R¹, R², R³, R⁴; andwherein preferably at least one of the groups R^(1′), R^(2′), R^(3′),R^(4′) is a polar group or polarising group and for the monomer group(K),

* represents a bond to another monomer unit having the Formula (A) or(K); and n′=1 to
 3. 7. A PAHC according to claim 6, comprising at least20 to 40% of monomer (A) and at least 60 to 80% of monomer (K), based onthe total of all monomer units (A) and (K) in the copolymer.
 8. A PAHCaccording to claim 6, wherein at least one of R^(1′), R^(2′), R^(3′),R^(4′) is a polar group or polarising group, and n=1 to
 20. 9. A PAHCaccording to claim 8, wherein one or 2 of the groups R^(1′), R^(2′),R^(3′), R^(4′) are selected from methoxy, cyanomethyl, CN and mixturesthereof, and n=1 to
 10. 10. A PAHC according to claim 6, furthercomprising one or more monomers (L), (M), (M′) and/or (N):

wherein each R^(1″), R^(2″), R^(3″), R^(4″), R^(5″), R^(6″) and R^(7″),each of which may be the same or different, is selected from the samegroup as R¹, R², R³, R⁴, R⁵, R⁶ and R⁷, as defined in claim 1; whereinn″=1 to 3; Ar₁, Ar₂ and Ar₃, which may be the same or different, eachrepresent, independently an optionally substituted C₆₋₄₀ aromatic group(mononuclear or polynuclear); and wherein monomer (A) is present in anamount of at least 20 wt. %; monomer (K) is present in an amount of atleast 60 wt. % and the remainder is comprised of monomers (L), (M), (M′)and/or (N), based on the total weight of all monomer units in thecopolymer.
 11. A Polycyclic Aromatic Hydrocarbon Copolymer (PAHC)comprising a mixture of at least one BXBX monomer unit having theFormula (A) and at least one monomer unit having the Formula (O/O′):

Formula (O/O′)-represents cis and/or trans-indenofluorene isomerswherein Y¹ and Y² are independently S or Se; k and l are independently 0or 1; wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ andR¹²; which may be the same or different, independently representshydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; a C₂-C₁₀ alkynyl groupsubstituted with a SiH₂R²² group, a C₂-C₁₀ alkynyl substituted with aSiHR²²R²³ group, or a C₂-C₁₀ alkynyl substituted with a—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group; wherein each R²² group isindependently selected from the group consisting of a branched orunbranched, substituted or unsubstituted C₁-C₁₀ alkyl group, a branchedor unbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₂-C₁₀ alkenyl group, and a substituted or unsubstitutedC₆-C₂₀ cycloalkylalkylene group; each R²³ group is independentlyselected from the group consisting of a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₁₀ alkenyl group, a substituted orunsubstituted C₂-C₂₀ cycloalkyl group, and a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group; R²⁴ is independentlyselected from the group consisting of hydrogen, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group, a substituted C₅-C₂₀ arylgroup, a substituted or unsubstituted C₆-C₂₀ arylalkylene group, anacetyl group, a substituted or unsubstituted C₃-C₂₀ heterocyclic ringcomprising at least one of O, N, S and Se in the ring; wherein x=1 or 2;y=1 or 2; z=0 or 1; and (x+y+z)=3; wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹and R²⁰ independently represent H or optionally substituted C₁-C₄₀carbyl or hydrocarbyl group optionally comprising one or moreheteroatoms; wherein R¹⁷ represents a halogen atom, H or optionallysubstituted C₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionallycomprising one or more heteroatoms; wherein k and l are independently 0or 1; wherein at least two of R¹, R³, R⁴, R⁶, R⁷, R⁹, R¹⁰, and R¹², area bond, represented by

*, to another monomer unit having the Formula (A) or (O); whereinmonomer (O/O′) is either the cis and/or trans-indenofluorene monomer andeach R^(1′), R^(2′), R^(3′) R^(4′), R^(5′), R^(6′), R^(7′), each ofwhich may be the same or different, is selected from the same group asR¹, R², R³, R^(4′) R⁶, R⁷ and wherein preferably at least one of thegroups, R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′) is apolar or polarising group and for the monomer group (O/O′)

* represents a bond to another monomer unit having the Formula (A) or(O/O′); and n′=1 to
 3. 12. A PAHC according to claim 11, comprising atleast 20 to 40% of monomer (A) and at least 60 to 80% of monomer (O),based on the total of all monomer units (A) and (O) in the copolymer.13. A PAHC according to claim 11, wherein for thecis/trans-indenofluorene monomer (O/O′), R^(1′), R^(2′), R^(3′), R^(4′),R^(5′), R^(6′), and R^(7′) which may be the same or different and atleast one wherein preferably at least one of R^(1′), R^(2′), R^(3′),R^(4′), R^(5′), R^(6′), and R^(7′) is substituted with at least onepolar group or more polarising group, and n=1 to
 20. 14. A PAHCaccording to claim 13, wherein one or 2 of the groups R^(1′), R^(2′),R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′) are selected from methoxy,cyanomethyl, CN and mixtures thereof, and n=1 to
 10. 15. A PAHCaccording to claim 11, further comprising one or more monomers (P), (Q)and/or (R):

wherein each R^(1″), R^(2″), R^(3″) and R^(4″), each of which may be thesame or different, is selected from the same group as R¹, R², R³ and R⁴,already defined above; Ar₁, Ar₂ and Ar₃, which may be the same ordifferent, each represent, independently an optionally substituted C₆₋₄₀aromatic group (mononuclear or polynuclear). Preferably at least one ofAr₁, Ar₂ and Ar₃ is substituted with at least one polar or morepolarising group, and n=1 to 20, preferably 1 to 10 and more preferably1 to
 5. Preferably, at least one of Ar₁, Ar₂ and Ar₃ is substituted with1, 2, 3, or 4, more preferably 1, 2 or 3, more preferably 1 or 2,preferably 1 polar or more polarising group(s); n″=1 to 3; and whereinmonomer (A) is present in an amount of at least 20 wt. %; monomer (O) ispresent in an amount of at least 60 wt. % and the remainder is comprisedof monomers (P), (Q) and/or (R), based on the total weight of allmonomer units in the copolymer.
 16. A PAHC according to claim 1, whereinR³═R¹⁰=a C₁ to C₁₄ alkyl group or optionally substituted C₁ to C₁₄ alkylgroup.
 17. A PAHC according to claim 1, wherein k=l=0 or
 1. 18.(canceled)
 19. A PAHC according to claim 1, wherein the copolymers havea number average molecular weight (Mn) of between 500 and 100,000.
 20. APAHC according to claim 1, wherein the copolymers are semiconductingcopolymers having a permittivity at 1000 Hz of greater than 1.5,preferably between 3.4 and
 8. 21. (canceled)
 22. A PAHC according toclaim 1, wherein at least one (and more preferably 2) of groups R¹, R⁶,R⁷, and R¹² are (tri-C₁₋₂₀ hydrocarbylsilyl) C₁₋₄ alkynyl groups,preferably (trihydrocarbylsilyl)ethynyl- groups. Preferably at least onepair of R¹/R⁶ and/or R⁷/R¹² are trihydrocarbylsilyl ethynyl groups. 23.A PAHC according to claim 1, wherein R¹, R³, R⁶, R⁷, R⁹ and R¹² arehydrogen.
 24. A PAHC according to claim 1, wherein—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) is selected from the group consisting oftrimethylsilyl, triethylsilyl, tripropylsilyl, dimethylethylsilyl,diethylmethylsilyl, dimethylpropylsilyl, dimethylisopropylsilyl,dipropylmethylsilyl, diisopropylmethylsilyl, dipropylethylsilyl,diisopropylethylsilyl, diethylisopropylsilyl, triisopropylsilyl,trimethoxysilyl, triethoxysilyl, triphenylsilyl, diphenylisopropylsilyl,diisopropylphenylsilyl, diphenylethylsilyl, diethylphenylsilyl,diphenylmethylsilyl, triphenoxysilyl, dimethylmethoxysilyl,dimethylphenoxysilyl, and methylmethoxyphenyl.
 25. A PAHC according toclaim 1, having the Formula (A1) or (A2)

wherein R²⁵, R²⁶ and R²⁷ are independently selected from the groupconsisting of C₁-C₆ alkyl and C₂-C₆ alkenyl, preferably independentlyselected from the group consisting of methyl, ethyl, propyl, isopropyl,n-butyl, isobutyl, t-butyl, 1-propenyl and 2-propenyl, more preferablyethyl, n-propyl and isopropyl;
 26. A PAHC according to claim 3, whereinthe one or more polar or polarising group(s) is independently selectedfrom the group consisting of nitro group, nitrile group, C₁₋₄₀ alkylgroup substituted with a nitro group, a nitrile group, a cyanate group,an isocyanate group, a thiocyanate group or a thioisocyanate group;C₁₋₄₀ alkoxy group optionally substituted with a nitro group, a nitrilegroup, a cyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; C₁₋₄₀ carboxylic acid group optionally substitutedwith a nitro group, a nitrile group, a cyanate group, an isocyanategroup, a thiocyanate group or a thioisocyanate group; C₂₋₄₀ carboxylicacid ester optionally substituted with a nitro group, a nitrile group, acyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; sulfonic acid optionally substituted with a nitrogroup, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; sulfonic acid esteroptionally substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; cyanate group, isocyanate group, thiocyanate group,thioisocyanate group; and an amino group optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; and combinations thereof.27. An organic semiconductor composition comprising a PAHC according toclaim 1 and a polyacene small molecule, wherein the PAHC has apermittivity at 1000 Hz of between 3.4 and 8.0 or between 3.4 and 4.5.28. (canceled)
 29. An organic semiconductor composition comprising aPolycyclic Aromatic Hydrocarbon Copolymer (PAHC) according to claim 1,wherein the composition has a permittivity at 1000 Hz of between 3 and6.5, between 3.4 and 8 or between 4 and 6.5.
 30. (canceled)
 31. Anorganic semiconductor composition according to claim 27 having a chargemobility value of at least 0.5 cm²V⁻¹s⁻¹, preferably between 2 and 5.0cm²V⁻¹s⁻¹.
 32. (canceled)
 33. An organic semiconductor compositionaccording to claim 27, wherein said composition is embedded in anelectronic device.
 34. An organic semiconductor composition according toclaim 33, wherein the electronic device is selected from organic fieldeffect transistors (OFETS), organic light emitting diodes (OLEDS),photodetectors, organic photovoltaic (OPV) cells, sensors, lasers,memory elements and logic circuits.
 35. An ink comprising a PAHCaccording to claim
 1. 36. A process for producing a Polycyclic AromaticHydrocarbon Copolymer (PAHC) comprising copolymerising a compositioncontaining at least one BXBX monomer unit selected from the structures(A′) and at least one arylamine monomer (B′):

wherein Y¹ and Y² are independently S or Se; k and l are independently 0or 1 wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ andR¹², which may be the same or different, independently representshydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; a C₂-C₁₀ alkynyl groupsubstituted with a SiH₂R²² group, a C₂-C₁₀ alkynyl substituted with aSiHR²²R²³ group, or a C₂-C₁₀ alkynyl substituted with a—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group; wherein each R²² group isindependently selected from the group consisting of a branched orunbranched, substituted or unsubstituted C₁-C₁₀ alkyl group, a branchedor unbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₂-C₁₀ alkenyl group, and a substituted or unsubstitutedC₆-C₂₀ cycloalkylalkylene group; each R²³ group is independentlyselected from the group consisting of a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₁₀ alkenyl group, a substituted orunsubstituted C₂-C₂₀ cycloalkyl group, and a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group; R²⁴ is independentlyselected from the group consisting of hydrogen, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group, a substituted C₅-C₂₀ arylgroup, a substituted or unsubstituted C₆-C₂₀ arylalkylene group, anacetyl group, a substituted or unsubstituted C₃-C₂₀ heterocyclic ringcomprising at least one of O, N, S and Se in the ring; wherein x=1 or 2;y=1 or 2; z=0 or 1; and (x+y+z)=3; wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹and R²⁰ independently represent H or optionally substituted C₁-C₄₀carbyl or hydrocarbyl group optionally comprising one or moreheteroatoms; wherein R¹⁷ represents a halogen atom, H or optionallysubstituted C₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionallycomprising one or more heteroatoms; wherein Ar₁, Ar₂ and Ar₃, which maybe the same or different, each represent, independently if in differentrepeat units, an optionally substituted C₆₋₄₀ aromatic group(mononuclear or polynuclear), wherein preferably at least one of Ar₁,Ar₂ and Ar₃ is substituted with at least one polar or more polarisinggroup; wherein X′ is a halogen atom or a cyclic borate group; andwherein Z′ is a halogen atom.
 37. (canceled)
 38. A process for producinga Polycyclic Aromatic Hydrocarbon Copolymer (PAHC) comprisingcopolymerising a composition containing at least one monomer unitselected from the structures (A′) and at least one monomer selected fromthe structure (K′):

wherein Y¹ and Y² are independently S or Se; k and l are independently 0or 1; wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ andR¹², which may be the same or different, independently representshydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; a C₂-C₁₀ alkynyl groupsubstituted with a SiH₂R²² group, a C₂-C₁₀ alkynyl substituted with aSiHR²²R²³ group, or a C₂-C₁₀ alkynyl substituted with a—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group; wherein each R²² group isindependently selected from the group consisting of a branched orunbranched, substituted or unsubstituted C₁-C₁₀ alkyl group, a branchedor unbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₂-C₁₀ alkenyl group, and a substituted or unsubstitutedC₆-C₂₀ cycloalkylalkylene group; each R²³ group is independentlyselected from the group consisting of a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₁₀ alkenyl group, a substituted orunsubstituted C₂-C₂₀ cycloalkyl group, and a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group; R²⁴ is independentlyselected from the group consisting of hydrogen, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group, a substituted C₅-C₂₀ arylgroup, a substituted or unsubstituted C₆-C₂₀ arylalkylene group, anacetyl group, a substituted or unsubstituted C₃-C₂₀ heterocyclic ringcomprising at least one of O, N, S and Se in the ring; wherein x=1 or 2;y=1 or 2; z=0 or 1; and (x+y+z)=3; wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹and R²⁰ independently represent H or optionally substituted C₁-C₄₀carbyl or hydrocarbyl group optionally comprising one or moreheteroatoms; wherein R¹⁷ represents a halogen atom, H or optionallysubstituted C₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionallycomprising one or more heteroatoms; wherein R^(1′), R^(2′), R^(3′),R^(4′) which may be the same or different, independently each represent,hydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; wherein preferably at leastone of R^(1′), R^(2′), R^(3′), R^(4′) is substituted with at least onepolar or more polarising group which is independently selected from thegroup consisting of nitro group, nitrile group, C₁₋₄₀ alkyl groupsubstituted with a nitro group, a nitrile group, a cyanate group, anisocyanate group, a thiocyanate group or a thioisocyanate group; a C₁₋₄₀alkoxy group optionally substituted with a nitro group, a nitrile group,a cyanate group, an isocyanate group, a thiocyanate group or athioisocyanate group; a C₁₋₄₀ carboxylic acid group optionallysubstituted with a nitro group, a nitrile group, a cyanate group, anisocyanate group, a thiocyanate group or a thioisocyanate group; a C₂₋₄₀carboxylic acid ester optionally substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; sulfonic acid optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; sulfonic acid esteroptionally substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; cyanate group, isocyanate group, thiocyanate group,thioisocyanate group; and an amino group optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; and combinations thereof;wherein at least one of R^(1′), R^(2′), R^(3′), R^(4′) groups is a polaror polarising group, and n=1 to 20; wherein X′ is a halogen atom or acyclic borate group; and wherein Z′ is a halogen atom.
 39. (canceled)40. A process for producing a Polycyclic Aromatic Hydrocarbon Copolymer(PAHC) comprising copolymerising a composition containing at least oneBXBX monomer unit selected from the structures (A′) and at least onemonomer (O′):

wherein Y¹ and Y² are independently S or Se; k and l are independently 0or 1 wherein each of R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹ andR¹², which may be the same or different, independently representshydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; a C₂-C₁₀ alkynyl groupsubstituted with a SiH₂R²² group, a C₂-C₁₀ alkynyl substituted with aSiHR²²R²³ group, or a C₂-C₁₀ alkynyl substituted with a—Si(R²²)_(x)(R²³)_(y)(R²⁴)_(z) group; wherein each R²² group isindependently selected from the group consisting of a branched orunbranched, substituted or unsubstituted C₁-C₁₀ alkyl group, a branchedor unbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₂-C₁₀ alkenyl group, and a substituted or unsubstitutedC₆-C₂₀ cycloalkylalkylene group; each R²³ group is independentlyselected from the group consisting of a branched or unbranched,substituted or unsubstituted C₁-C₁₀ alkyl group, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₁₀ alkenyl group, a substituted orunsubstituted C₂-C₂₀ cycloalkyl group, and a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group; R²⁴ is independentlyselected from the group consisting of hydrogen, a branched orunbranched, substituted or unsubstituted C₂-C₁₀ alkynyl group, asubstituted or unsubstituted C₂-C₂₀ cycloalkyl group, a substituted orunsubstituted C₆-C₂₀ cycloalkylalkylene group, a substituted C₅-C₂₀ arylgroup, a substituted or unsubstituted C₆-C₂₀ arylalkylene group, anacetyl group, a substituted or unsubstituted C₃-C₂₀ heterocyclic ringcomprising at least one of O, N, S and Se in the ring; wherein x=1 or 2;y=1 or 2; z=0 or 1; and (x+y+z)=3; wherein each of R¹⁵, R¹⁶, R¹⁸, R¹⁹and R²⁰ independently represent H or optionally substituted C₁-C₄₀carbyl or hydrocarbyl group optionally comprising one or moreheteroatoms; wherein R¹⁷ represents a halogen atom, H or optionallysubstituted C₁-C₄₀ carbyl or C₁-C₄₀ hydrocarbyl group optionallycomprising one or more heteroatoms; wherein k and l are independently 0or 1; wherein R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), R^(6′) and R^(7′)which may be the same or different, independently each represent,hydrogen; a branched or unbranched, substituted or unsubstituted C₁-C₄₀alkyl group; a branched or unbranched, substituted or unsubstitutedC₂-C₄₀ alkenyl group; a branched or unbranched, substituted orunsubstituted C₂-C₄₀ alkynyl group; an optionally substituted C₃-C₄₀cycloalkyl group; an optionally substituted C₆-C₄₀ aryl group; anoptionally substituted C₁-C₄₀ heterocyclic group; an optionallysubstituted C₁-C₄₀ heteroaryl group; an optionally substituted C₁-C₄₀alkoxy group; an optionally substituted C₆-C₄₀ aryloxy group; anoptionally substituted C₇-C₄₀ alkylaryloxy group; an optionallysubstituted C₂-C₄₀ alkoxycarbonyl group; an optionally substitutedC₇-C₄₀ aryloxycarbonyl group; a cyano group (—CN); a carbamoyl group(—C(═O)NR¹⁵R¹⁶); a carbonyl group (—C(═O)—R¹⁷); a carboxyl group(—CO₂R¹⁸) a cyanate group (—OCN); an isocyano group (—NC); an isocyanategroup (—NCO); a thiocyanate group (—SCN) or a thioisocyanate group(—NCS); an optionally substituted amino group; a hydroxy group; a nitrogroup; a CF₃ group; a halo group (Cl, Br, F, I); —SR¹⁹; —SO₃H; —SO₂R²⁰;—SF₅; an optionally substituted silyl group; wherein preferably at leastone of R^(1′), R^(2′), R^(3′), R^(4′), R^(5′), and R^(7′) is substitutedwith at least one polar or more polarising group which is independentlyselected from the group consisting of nitro group, nitrile group, C₁₋₄₀alkyl group substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; a C₁₋₄₀ alkoxy group optionally substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; a C₁₋₄₀ carboxylic acid group optionallysubstituted with a nitro group, a nitrile group, a cyanate group, anisocyanate group, a thiocyanate group or a thioisocyanate group; a C₂₋₄₀carboxylic acid ester optionally substituted with a nitro group, anitrile group, a cyanate group, an isocyanate group, a thiocyanate groupor a thioisocyanate group; sulfonic acid optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; sulfonic acid esteroptionally substituted with a nitro group, a nitrile group, a cyanategroup, an isocyanate group, a thiocyanate group or a thioisocyanategroup; cyanate group, isocyanate group, thiocyanate group,thioisocyanate group; and an amino group optionally substituted with anitro group, a nitrile group, a cyanate group, an isocyanate group, athiocyanate group or a thioisocyanate group; and combinations thereof;wherein X′ is a halogen atom or a cyclic borate group; and wherein Z′ isa halogen atom. 41-42. (canceled)
 43. An organic semiconductorcomposition according to claim 27, wherein said composition is embeddedin an organic semiconductor layer.